Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 10.3 - 15.2 GPa | 1500 - 2200 ksi | Average value: 13.0 GPa Grade Count:6 |
Overview of materials for Polyetherimide (PEI), 40% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 40% Glass Fiber". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Modulus of Elasticity | 10.3 - 35.0 GPa | 1500 - 5080 ksi | Average value: 19.5 GPa Grade Count:27 |
Overview of materials for Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler". Specific grades with carbon fiberr content be.. |
|||
Modulus of Elasticity | 10.3 - 28.0 GPa | 1500 - 4060 ksi | Average value: 20.3 GPa Grade Count:39 |
Overview of materials for Nylon 66, 60% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. .. |
|||
Modulus of Elasticity | 10.3 GPa | 1500 ksi | Parallel |
Momentive Performance Materials BNC1 Boron Nitride (BN) Refractory Composite Boron Nitride is a unique engineering material. It is a soft, machinable ceramic which can be combined with other refractory ceramics including Aluminum Oxide, Silicon Nitride, Aluminum Nitride, Mu.. |
|||
Modulus of Elasticity | 10.3 - 11.7 GPa | 1500 - 1700 ksi | ASTM D638 |
Premix Premi-Glas® 1200H-24 Polyester SMC
(discontinued **) Premi-Glas® 1200H-24 is a 24% fiberglass reinforced, thermoset, Sheet Molding Compound designed for applications where arc resistance and dielectric strength are required and UL 94 HB flame recogni.. |