Polymer Property : Modulus of Elasticity = 10.3 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Modulus of Elasticity 10.3 - 15.2 GPa
1500 - 2200 ksi
Average value: 13.0 GPa Grade Count:6
Overview of materials for Polyetherimide (PEI), 40% Glass Fiber
This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 40% Glass Fiber". Specific grades with glass content between 35% and 44% are included. E..
Modulus of Elasticity 10.3 - 29.0 GPa
1490 - 4210 ksi
Average value: 15.2 GPa Grade Count:8
Overview of materials for Phenolic, Novolac, Mineral/Graphite Filled
This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Graphite Filled". Each property range of values reported is minimum and maxim..
Modulus of Elasticity 10.3 - 35.0 GPa
1500 - 5080 ksi
Average value: 19.5 GPa Grade Count:27
Overview of materials for Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 10% Carbon Fiber Filler". Specific grades with carbon fiberr content be..
Modulus of Elasticity 10.3 - 28.0 GPa
1500 - 4060 ksi
Average value: 20.3 GPa Grade Count:39
Overview of materials for Nylon 66, 60% Glass Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 60% Glass Fiber Filled". Specific grades with glass content between 55% and 64% are included. ..
Modulus of Elasticity 10.3 GPa
1500 ksi
Parallel
Momentive Performance Materials BNC1 Boron Nitride (BN) Refractory Composite
Boron Nitride is a unique engineering material. It is a soft, machinable ceramic which can be combined with other refractory ceramics including Aluminum Oxide, Silicon Nitride, Aluminum Nitride, Mu..
Modulus of Elasticity 10.3 GPa
1490 ksi
ISO 527
GEHR Plastics PEEK-30GF Polyetheretherketone, 30% Glass Fiber
Polyether etherketone can be used at very high temperatures and it shows a good mechanical strength, toughness, hardness, flexural strength, and torsional strength. PEEK exhibits excellent chemical ..
Modulus of Elasticity 10.3 - 11.7 GPa
1500 - 1700 ksi
ASTM D638
Premix Premi-Glas® 1200H-24 Polyester SMC  (discontinued **)
Premi-Glas® 1200H-24 is a 24% fiberglass reinforced, thermoset, Sheet Molding Compound designed for applications where arc resistance and dielectric strength are required and UL 94 HB flame recogni..