Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Modulus of Elasticity | 8.50 - 22.0 GPa | 1230 - 3190 ksi | Average value: 12.6 GPa Grade Count:21 |
Overview of materials for Liquid Crystal Polymer (LCP), Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Liquid Crystal Polymer (LCP), Mineral Filled". Each property range of values reported is minimum and max.. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | |
Lehmann & Voss LUVOCOM® 3/CF/10/BK Polyamide 6, with carbon fiber Applications: Automotive industry, textile machinery, apparatus- and precision engineering.High-strength and stiff parts; low coefficient of expansion.dynamic stressElectrically conductive, suitable.. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | |
Lehmann & Voss LUVOCOM® 50-7154 Polycarbonate, with carbon fiber, low-warpage Applications: Data processing machinery, precision engineering, film and photo industry, sporting and leisure goods, medical enineering.Strong, stiff parts.Reduced moment of inertia compared with me.. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | |
Lehmann & Voss LUVOCOM® 1105-7583 PEEK, with glass fiber and PTFE, improved wear resistance Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Good friction and wear behaviour especially at increased temperatures.Chemical and hydroly.. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | |
Mo-Sci Corporation GL-0271 E-Glass Spheres Appearance: Solid low alkali E-glass beads with greenish color.Chemical Durability: Weight loss @ 90°C for 24 hrs in 5% HCl 0.3 mg/cm2Information provided by Mo-Sci Corporation. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | ISO 527-2 |
Tisan TISLAMID® 66 25% Glass Fiber Reinforced Flame Retardant (V0). Heat Stabilized Nylon 66 TISLAMID has a wide area of application in electric/electronic, automotive, durable goods and telecommunications industries. It demonstrates characteristics such as Excellent chemical resistanceElec.. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | ISO 527-1/-2 |
BASF Ultramid® B3WGM 24 HP BK 23210 10/20% Glass/Mineral Filled PA6-1 (Dry) Description: 20% mineral-filled and 10% glass-fiber reinforced injection-molding grade with outstanding flowability for technical parts with medium rigidity and high dimensional stability, e.g. for.. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | ISO 178 |
Addiplast Addinyl A2H V25 Flame Retardant Nylon 66, 25% Glass Filled Flame retardant, 25% glass fiber reinforced, with halogensInformation provided by Addiplast. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | ISO 527 |
BASF Ultramid® A3EG7 35% Glass Filled PA66 (Conditioned) Ultramid A3EG6 is a 35% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | ISO 527 |
BASF Ultramid® A3X2G7 35% Glass Filled PA66 (Conditioned) Ultramid A3X2G7 is a 35% glass fiber reinforced injection molding PA66 grade with improved flame retardance and enhanced long-term stability. Flame retardant based on red phosphorus; very high stif.. |
|||
Modulus of Elasticity | 8.50 GPa | 1230 ksi | ISO 527-2 |
BASF Ultradur® B 4330 G6 HR 30% Glass Filled PBT Description: Is a PBT-I, injection-molding grade with 30% glass fibers, for rigid, tough and dimensionally stable technical parts with increased requirements on hydrolysis resistance and toughness, .. |