Polymer Property : Compressive Strength = 580 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Strength 4.00 MPa
580 psi
1% strain over 1000 hours; ISO.899 DIN.53444
Omnia Plastica PA 11 Rilsan B
The only engineering plastic of natural origin (derived from castor oil), it is a polyamide which, unlike the other nylons, does not absorb humidity. It has all the good mechanical features of polya..
Compressive Strength 4.00 MPa
580 psi
1% strain over 1000 hours; ISO.899 DIN.53444
Omnia Plastica PP Polypropylene
The mechanical features of PP are better than those of PE H.D. It withstands attack by alkali and acids and consequently it is widely used for components in the chemical industry when a moderate str..
Compressive Strength >= 4.00 MPa
>= 580 psi
Perpendicular to holes
MarkeTech H-2 Honeycomb Ceramic
MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and lo..
Compressive Strength >= 4.00 MPa
>= 580 psi
Perpendicular to holes
MarkeTech H-3 Honeycomb Ceramic
MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and lo..
Compressive Strength >= 4.00 MPa
>= 580 psi
Perpendicular to holes
MarkeTech H-4 Honeycomb Ceramic
MarkeTech International special honeycomb ceramics have a uniform lattice structure, low expansion coefficient, good thermal shock resistance, higher specific surface area, low-pressure drop, and lo..
Compressive Strength 4.00 - 6.00 MPa
580 - 870 psi
Cold Crushing Strength
Gouda Vuurvast GI 28 Insulating Refractory Brick
This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast.
Compressive Strength 4.00 - 6.00 MPa
580 - 870 psi
Cold Crushing Strength
Gouda Vuurvast GI 26 Insulating Refractory Brick
This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast.
Compressive Strength 4.00 MPa
580 psi
Dried at 110°C (230°F)
Skamol Group VERMICAST 14-100 Insulating Castable
SKAMOL insulating castables have the following characteristics: Max. service temperature: Up to 1100°C (2102°F)Back-up insulation or hot-face usesFor casting and gunningProducts are based on f..
Compressive Strength 4.00 MPa
580 psi
Thermal Ceramics TC-26 HS High Temperature Insulating Firebrick
The bond developed is a ceramic bond that is formed by high temperature firing. This produces bricks that are very stable and strong at temperatures higher than 2600°F (1427°C). Features:High temp..
Compressive Strength 4.00 MPa
580 psi
In the In Plane Direction
Cymat A35620SC 030SS Stabilized Aluminum Foam
Description: Cymat A35620SC 030SS stabilized aluminum foam (SAF) is a closed cell aluminum foam formed from A356 aluminum alloy with a density of 0.3 g/cm3. The mechanical properties of SAF make it ..
Compressive Strength 4.00 MPa
580 psi
Upper Yield in the Through Plane Direction
Cymat A35620SC 040SS Stabilized Aluminum Foam
Description: Cymat A35620SC 040SS stabilized aluminum foam (SAF) is a closed cell aluminum foam formed from A356 aluminum alloy with a density of 0.4 g/cm3. The mechanical properties of SAF make it ..
Compressive Strength 4.00 MPa
580 psi
Cold Crush Strength; ASTM C133
BNZ Materials BNZ-26 HS Insulating Firebrick
BNZ produces many types of Insulating Fire Brick (IFB) for use in applications from 2,000°F (1,093°C) to 3,200°F (1,760°C). Each type is formulated to meet specific thermal and physical requirem..
Compressive Strength 4.00 MPa
580 psi
Cold Crush Strength; ASTM C133
BNZ Materials Color B Insulating Firebrick (French Grade)
BNZ produces many types of Insulating Fire Brick (IFB) for use in applications from 2,000°F (1,093°C) to 3,200°F (1,760°C). Each type is formulated to meet specific thermal and physical requirem..