Polymer Property : Compressive Strength = 870 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Compressive Strength 4.00 - 6.00 MPa
580 - 870 psi
Cold Crushing Strength
Gouda Vuurvast GI 28 Insulating Refractory Brick
This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast.
Compressive Strength 4.00 - 6.00 MPa
580 - 870 psi
Cold Crushing Strength
Gouda Vuurvast GI 26 Insulating Refractory Brick
This data represents average values, obtained from samples that were cut from standard bricks.Information provided by Gouda Vuurvast.
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin NEOFLON AP-210AS PFA Pellets
NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Anti-static grader for injection molding.Information provided by D..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin NEOFLON AP-230ASL PFA Pellets
NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Anti-static grader for extrusion molded parts. Piping, tube, etc...
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin NEOFLON NP-101 FEP Pellets
NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: High speed wire and cable coatings.Information pro..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin NEOFLON NP-120 FEP Pellets
NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: Heavy wall wire insulation, cable jacketing, tubes..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin NEOFLON NP-130 FEP Pellets
NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion.Applications: Heavy wall wire insulation, cable jacketing, pipe, shrinka..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin NEOFLON NP-30 FEP Pellets
NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion molding.Applications: Heavy wall wire insulation, tubes, cable jacketing..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON F-104 PTFE Fine Powder
Processing Methods: Paste extrusion, calendering.Applications: Unsintered tape, sealing tape, low specific gravity tape, tape for wrapping flat cables, tubes.Information provided by Daikin Industrie..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON F-201 PTFE Fine Powder
Processing Methods: Paste extrusion.Applications: Spaghetti tubes, small diameter tubes, fine electric wire smaller than AGW16.Information provided by Daikin Industries.
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON F-205 PTFE Fine Powder
Processing Methods: Paste extrusion.Applications: Spaghetti tubes, small diameter tubes, fine electric wire smaller than AGW16.Information provided by Daikin Industries.
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON M-111 PTFE Molding Powder, Fine Cut
Fine cut powder.Processing Methods: Compression molding.Features: Produces moldings with extremely smooth and fine surface. Suited to making packing and gaskets since moldings have an especially go..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON M-139 PTFE Molding Powder, Free Flow
Free flow powder.Processing Methods: Compression molding and automatic compression molding.Features: Excellent fluidity. Apparent density is large and ideal for automated compression molding proces..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON M-18 PTFE Molding Powder, Fine Cut
Fine cut powder.Processing Methods: Compression molding.Features: Suited to molding of large billets, has nearly the same molding characteristics of M-12. Also allows uniform mixing of inorganic fi..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON M-391 PTFE Molding Powder, Free Flow
Free flow powder.Processing Methods: Compression molding and automatic or semi-automatic compression molding.Features: Used if concerned about insufficient molding pressure for flat sheets.Informati..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON M-392 PTFE Molding Powder, Free Flow
Free flow powder.Processing Methods: Compression molding, automatic or semi-automatic compression molding, isostatic molding, and ram extrusion.Features: Good fill characteristics particularly into ..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON M-393 PTFE Molding Powder, Free Flow
Free flow powder.Processing Methods: Compression molding, automatic compression molding, and ram extrusion.Features: Maximum emphasis given to ease of handling during molding. Used when molded arti..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-1030 PTFE 15% Glass Fiber Filled Molding Powder
15% glass fiber filled. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Available in all forms (e.g. bearings, gaskets, valve seats,..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-1040 PTFE 20% Glass Fiber Filled Molding Powder
20% glass fiber filled. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Available in all forms (e.g. bearings, gaskets, valve seats,..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-1050F PTFE 25% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow
25% glass fiber filled. High apparent density and free-flowing properties. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Availabl..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-1241F PTFE 20% Glass Fiber and 5% Graphite Filled Molding Powder, High Apparent Density, Free Flow
20% glass fiber and 5% graphite filled. High apparent density and free-flowing properties. High wear resistance, low friction, high creep resistance.Applications: Mechanical and chemical service (..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-2030 PTFE 15% Graphite Filled Molding Powder
15% graphite filled. Low friction, excellent chemical resistance, high creep resistance.Applications: Mechanical and chemical service (e.g. bearings, gaskets, packings)Information provided by Daiki..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-2060 PTFE 30% Graphite Filled Molding Powder
30% graphite filled. Low friction, excellent chemical resistance, high creep resistance.Applications: Mechanical and chemical service (e.g. bearings, gaskets, packings)Information provided by Daiki..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-6030 PTFE 15% Carbon Fiber Filled Molding Powder
15% carbon fiber filled. High wear resistance, high load resistance, high bend resistance.Applications: Mechanical service (e.g. bearings, mechanical seals and bearing pads)Information provided by ..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-6030F PTFE 15% Carbon Fiber Filled Molding Powder, High Apparent Density, Free Flow
15% carbon fiber filled. High apparent density and free-flowing properties. High wear resistance, high load resistance, high bend resistance.Applications: Mechanical service (e.g. bearings, mechan..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin NEOFLON AP-210 PFA Pellets
NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Injection molded parts, wire insulation, etc.Information provided ..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin NEOFLON AP-230 PFA Pellets
NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Linings, tubing, etc.Information provided by Daikin Industries.
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin NEOFLON NP-3000 FEP Pellets
NEOFLON FEP molding materials are supplied as translucent white pellets for melt flow processes.Processing Methods: Extrusion.Applications: Ultra high speed wire and cable coatings.Information provi..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-1030F PTFE 15% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow
15% glass fiber filled. High apparent density and free-flowing properties. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Availabl..
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Daikin POLYFLON MG-1050 PTFE 25% Glass Fiber Filled Molding Powder
25% glass fiber filled. High wear resistance, low friction, good electrical properties.Applications: Mechanical and electrical service. Available in all forms (e.g. bearings, gaskets, valve seats,..