Polymer Property : Compressive Strength = 19600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Compressive Strength	135 MPa	19600 psi	Test specimen flat tested; ISO 604
Hexion Bakelite™ PF 13 Phenolic Formaldehyde Resin, UL Listed (discontinued **) Phenolic molding compound, inorganically mica filled, heat resistance, good electrical properties, UL listed molding compound 0.75 mm/V-1 (NC), 3 mm/V-0, standardized molding compound.Application ar..
Compressive Strength	135 MPa @Strain 3.50 %	19600 psi @Strain 3.50 %	DIN EN ISO 604
Wolf Kunststoff ZEDEX® ZX-410 A4A Polymer Alloy ZX-410 is a bearing material with excellent properties and a very affordable price.Main Characteristics: Hard, Stiff, Tough; High dimensional stability; High chemical resistance; High water resistan..
Compressive Strength	135 MPa	19600 psi	DIN EN ISO 604
Wolf Kunststoff ZEDEX® ZX-410V7T A4T Polymer Alloy, Fiber Reinforced, Friction Modified Main Characteristics: Fiber-reinforced; Friction-modified; Very high stiffness (higher than that of fiber-reinforced PEEK); Very low thermal expansion coefficient; Low friction; High wear resistance..
Compressive Strength	135 MPa	19600 psi	ASTM D695
Unitika UNILATE® 1 PC PET Standard gradeUNILATE® products are plate materials prepared by using a polyethylene terephthalate (PET resin) as the main component, blending it with glass staple fiber, inorganic filler, and othe..
Compressive Strength	135 - 163 MPa	19600 - 23600 psi
Bulk Molding Compounds BMC G10(12) Mineral Filled, Glass Fiber Reinforced Polyester BMC G10 is a general purpose, mineral filled, glass fiber-reinforced polyester that is suitable for compression, transfer and stuffer injection molding. G10 is well suited to applications where hig..
Compressive Strength	135 MPa	19600 psi
Ohio Carbon Blank OCB TTK-4 EDM Grade Graphite Available in a range of sizes and shapes.