Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Compressive Strength | 14.0 MPa | 2030 psi | 1% strain over 1000 hours; ISO.899 DIN.53444 |
Omnia Plastica Akulon® POM h Acetal Homopolymer The general features of homopolymer acetalic resin are similar to those of copolymer POM c, except that service temperature (under load) is slightly higher but resistance to hydrolysis and strong al.. |
|||
Compressive Strength | 14.0 MPa | 2030 psi | 1% strain over 1000 hours; ISO.899 DIN.53444 |
Omnia Plastica Arnite Omnialite POM c Acetal Copolymer Polyoxymethylene, commonly called Acetal, is a crystalline polymer obtained from the polymerisation of formaldehyde. Discovered fairly recently (1960), it has enjoyed rapid growth and large acceptan.. |
|||
Compressive Strength | 14.0 MPa | 2030 psi | Elastic Limit |
Wolf Kunststoff ZEDEX® ZX-100EL55 A1F Polymer Alloy, Elastomer Modified Main Characteristics: Rubbery; Soft; High shock absorption; High impact resistance; Elongation > 300%Applications: Handling, Vessel and Pump, Steel and Water, Chemical Engineering, Automitve Technol.. |
|||
Compressive Strength | 14.0 - 20.0 MPa | 2030 - 2900 psi | ASTM D695 |
Arkema Group KYNAR FLEX® 2500-20 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. Highest flexibility. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechanical st.. |