Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength | >= 12.6 MPa | >= 1820 psi | NBR NM-IEC 60811-1-1 |
Karina Karintox 70 Polyolefin Compound Halogen free, fire retardant, low smoke and fume polyolefinic compound. Recommended for insulation of electrical cables up to 1KV.Information provided by Karina Indústria e Comércio de Plá.. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | NBR NM-IEC 60811-1-1 |
Karina Karintox 70/2 Polyolefin Compound Halogen free, fire retardant, low smoke and fume polyolefinic compound. Recommended for insulation of electrical cables up to 1KV.Information provided by Karina Indústria e Comércio de Plá.. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | NBR NM-IEC 60811-1-1 |
Karina Karintox 70/6 Polyolefin Compound Karintox is a thermoplastic polyolefin, flame retardant, non-halogen, and low smoke emission. Recommended for electrical coating for cables until 1KV. For a better usage/processing, manufacturer sug.. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | ASTM D 638 |
Karina 752D48/1-C-IS-BZ Black PVC Compound Heavy metal free PVC compound recommended for extrusion of automotive profiles.Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | ASTM D 638 |
Karina 801-08/98-C-IS Beige PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | ASTM D 638 |
Karina 801-10/49-C-IS White PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | ASTM D 638 |
Karina 801-18/489-C-IS Gray PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | NBR NM-IEC 60811-1-1 |
Karina 809D48/1-C-IS-LMP Black PVC Compound Heavy metal free PVC compound recommended for extrusion of coaxial cables jacket. Also recommended for extrusion of automotive flexible tube. Working temperature range: -40°C to +80°C.Inform.. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | After 168H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
Karina 809D48/1-C-IS-LMP Black PVC Compound Heavy metal free PVC compound recommended for extrusion of coaxial cables jacket. Also recommended for extrusion of automotive flexible tube. Working temperature range: -40°C to +80°C.Inform.. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | NBR NM-IEC 60811-1-1 |
Karina 880-18/402-F-AC Gray PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | After 168 H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
Karina 880-18/402-F-AC Gray PVC Compound Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | NBR NM-IEC 60811-1-1 |
Karina 951-35/4-IS-LMP Ivory PVC Compound Heavy metal free PVC compound with high electrical insulation resistance. Recommended for insulation of CI and CCI cables.Information provided by Karina Indústria e Comércio de Plásticos Lt.. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | After 168 H in Air Oven at 100°C; NBR NM-IEC 60811-1-2 |
Karina 951-35/4-IS-LMP Ivory PVC Compound Heavy metal free PVC compound with high electrical insulation resistance. Recommended for insulation of CI and CCI cables.Information provided by Karina Indústria e Comércio de Plásticos Lt.. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | NBR NM-IEC 60811-1-1 |
Karina 70900-35/1-E-AC Ivory PVC Compound Flame retardant PVC compound, class 70C (PVC/A), recommended for insulation of electrical wires and cables (BWF).Information provided by Karina Indústria e Comércio de Plásticos Ltda. |
|||
Tensile Strength | >= 12.6 MPa | >= 1820 psi | After 168H in air oven at 100°C; NBR NM-IEC 60811-1-2 |
Karina 70900-35/1-E-AC Ivory PVC Compound Flame retardant PVC compound, class 70C (PVC/A), recommended for insulation of electrical wires and cables (BWF).Information provided by Karina Indústria e Comércio de Plásticos Ltda. |