Physical Properties | Metric | English | Comments |
---|---|---|---|
Melt Flow | 5.4 - 9.0 g/10 min @Load 21.6 kg, Temperature 190 °C |
5.4 - 9.0 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@5kg ratio > 18; ASTM D1283 |
NIZHNEKAMSKNEFTEKHIM PE 6250D (506H4) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
Melt Flow | 6.0 - 9.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
6.0 - 9.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
±15% |
Kazanorgsintez PE2NT22-12 High Density Polyethylene Composite Production Method: Copolymerization of eythylene at low pressure in presence of complex catalysts using gaseous-phase method. Application: Composition is intended for injection molding processin.. |