- Polymer Property : Melt Flow = 1.2 g/10 min
Polymer Property : Melt Flow = 1.2 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| NIZHNEKAMSKNEFTEKHIM PE 4115N (16401) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| NIZHNEKAMSKNEFTEKHIM PE 4116N (16401) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| NIZHNEKAMSKNEFTEKHIM PE 4117N (18401) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| NIZHNEKAMSKNEFTEKHIM PE 5117N (18601) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| NIZHNEKAMSKNEFTEKHIM PE 5118N (18601) Linear Low Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| NIZHNEKAMSKNEFTEKHIM PE 4550N (50401M) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
| Melt Flow | 0.80 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.80 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| NIZHNEKAMSKNEFTEKHIM PE 4650N (50401N) High Density Polyethylene Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer |
|||
| Melt Flow | 0.70 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
±10% |
| Kazanorgsintez PE2NT 15-10 Linear Low Density Polyethylene Production Method: Gaseous-phase method. Application: Composition is intended to be processed into a stretch film.Information Provided by Kazanorgsintez |
|||
| Melt Flow | 0.70 - 1.2 g/10 min @Load 2.16 kg, Temperature 190 °C |
0.70 - 1.2 g/10 min @Load 4.76 lb, Temperature 374 °F |
±10% |
| Kazanorgsintez PE2NT 15-5 Linear Low Density Polyethylene Production Method: Gaseous-phase method. Application: Composition is intended to be processed into a stretch film.Information Provided by Kazanorgsintez |
|||