Physical Properties | Metric | English | Comments |
---|---|---|---|
Thickness | 13.0 microns | 0.512 mil | printed through a 230 mesh SS screen with 13 micron emulsion back off |
Gwent Electronic Materials C10903P14 Carbon/Graphite Ink Carbon Graphite Ink is used for screen printing working electrodes. This is a carbon graphite ink, which has been optimized to give superior electrochemical performance with good reversibility when.. |
|||
Thickness | 13.0 microns | 0.512 mil | Cured, Typical, Using a 156 mesh stainless steel screen, 13 micron emulsion |
Gwent Electronic Materials C2090225D7 Silver/Silver Chloride Paste Silver/Silver Chloride Paste has a ratio of Silver to Silver Chloride of 70/30. The paste is in a ready to use form at a viscosity suitable for automatic or semi-automatic screen printing. The paste.. |
|||
Thickness | 13.0 microns | 0.512 mil | when printed through a 156 mesh |
Gwent Electronic Materials C61003P7 Silver / Silver Chloride Paste C61003P7 has a ratio of Silver to Silver Chloride of 60/40. This is used for reference electrodes in Medical Diagnostics, Environmental Sensor and the "Agri-Food" Industries. It forms part of a fa.. |
|||
Thickness | 13.0 - 15.0 microns | 0.512 - 0.591 mil | Gauge |
UBE 1024FDX41 Nylon 6 BOPA Film Specialties: Excellent processing stabilityProcessing: Best for BOPAApplications: BOPA film (T-die)Information provided by UBE. |
|||
Thickness | 13.0 microns | 0.512 mil | |
Dow LDPE 752A Low Density Polyethylene, Film Grade DOW LDPE 752A resin is a drawdown film resin for thin gauge applications such as garment films. It contains high levels of both slip and antiblock additives. This material complies with U.S.FDA regu.. |
|||
Thickness | 13.0 microns | 0.512 mil | Upward surface, as processed; Mitutoyo Surftest-402 |
3D Systems CastForm™ PS Plastic for SLS® Systems For use with all selective laser sintering (SLS®) systems.ApplicationsCreate patterns directly rather than through indirect methodsComplex investment casting patternsReactive metals like titaniumLo.. |