Polymer Property : Melt Index of Compound = 150 g/10 min Product List

Physical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Physical Properties	Metric	English	Comments
Melt Index of Compound	150 g/10 min @Load 2.16 kg, Temperature 190 Â°C	150 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
ICO Polymers ICOFLOâ„¢ 510-5005 1000 Micron EVA Powder Description: ICOFLO 510-5005 is an EVA powder specifically designed to be used in the preparation of masterbatch (concentrate). By utilizing a free flowing powder as a carrier in masterbatch (inste..
Melt Index of Compound	150 g/10 min @Load 2.16 kg, Temperature 190 Â°C	150 g/10 min @Load 4.76 lb, Temperature 374 Â°F	ASTM D1238
ICO Polymers ICOTEXâ„¢ 520-5005 1000 Micron EVA Powder Description: ICOTEX 520-5005 is an EVA powder that has been developed to meet the special requirements of the textile coating industry. Key Characteristics: very high melt flow, fast melting, great ..
Melt Index of Compound	150 g/10 min @Load 21.6 kg, Temperature 190 Â°C	150 g/10 min @Load 47.6 lb, Temperature 374 Â°F	cm<sup>3</sup>/10 min
Huntsman IROGRANÂ® A 85 P 4854 Ether-Based TPU-For Cable Industry Introduction: IROGRAN A 85 P 4854 is a flame-retardant, halogen-free polyether based thermoplastic polyurethane intended for extrusion and injection molding applications. IROGRAN A 85 P 4854 is part..
Melt Index of Compound	150 - 200 g/10 min @Load 2.16 kg, Temperature 190 °C	150 - 200 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group LOTRYL® 28 BA 175 Copolymer Ethylene - Butyl Acrylate LOTRYL® 28 BA 175 is a random copolymer of ethylene and butyl acrylate, prepared by the high pressure polymerization process. Co-monomer content is 28% in weight. LOTRYL® 28 BA 175 is particularly..
Melt Index of Compound	150 - 200 g/10 min @Load 2.16 kg, Temperature 190 °C	150 - 200 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group LOTRYL® 37 EH 175 Copolymer Ethylene - 2-Ethylhexyl Acrylate LOTRYL® 37EH175 is a random copolymer of Ethylene and 2-Ethylhexyl Acrylate, prepared by the high pressure polymerization process. LOTRYL® 37EH175 is particularly recommended for the formulation o..
Melt Index of Compound	150 - 210 g/10 min @Load 2.16 kg, Temperature 190 °C	150 - 210 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
Arkema Group OREVAC® 9305 EVA Terpolymer OREVAC® is a range of ethylene-vinyl acetate copolymers modified by adjunction of polar groups which, when molten, have excellent adhesive properties to various substrates. They are supplied as fre..