Physical Properties | Metric | English | Comments |
---|---|---|---|
Linear Mold Shrinkage, Transverse | 0.0092 - 0.0094 cm/cm @Time 86400 sec |
0.0092 - 0.0094 in/in @Time 24.0 hour |
ASTM D 955 |
SABIC Innovative Plastics LNP Thermocomp OB008 PPS - Branched LNP* Thermocomp* OB008 is a compound based on Branched PPS containing Glass Beads.This data was supplied by SABIC-IP for the Americas region. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0094 cm/cm @Thickness 3.20 mm |
0.0075 - 0.0094 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Valox® V4860HR PBT (Asia Pacific) 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified. |
|||
Linear Mold Shrinkage, Transverse | 0.0075 - 0.0094 cm/cm @Thickness 3.20 mm |
0.0075 - 0.0094 in/in @Thickness 0.126 in |
SABIC Method |
SABIC Innovative Plastics Valox® V4860HR PBT (Europe-Africa-Middle East) 30% glass reinforced PBT, UL94 V-0 rated, Hydrolytically stable, Impact Modified. |