SABIC Innovative Plastics LNP Thermocomp OB008 PPS - Branched
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp OB008 PPS - Branched.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Thermocomp* OB008 is a compound based on Branched PPS containing Glass Beads.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| 1.635 g/cc | 0.05907 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.010 % | 0.010 % | 23°C / 50% RH; ISO 62 |
| 0.010 % @Time 86400 sec |
0.010 % @Time 24.0 hour |
50% RH; ASTM D 570 | |
| Linear Mold Shrinkage, Flow | 0.0092 - 0.0094 cm/cm @Time 86400 sec |
0.0092 - 0.0094 in/in @Time 24.0 hour |
ASTM D 955 |
| Linear Mold Shrinkage, Transverse | 0.0092 - 0.0094 cm/cm @Time 86400 sec |
0.0092 - 0.0094 in/in @Time 24.0 hour |
ASTM D 955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D 638 |
| 46.0 MPa | 6670 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | Type I, 5 mm/min; ASTM D 638 |
| 47.0 MPa | 6820 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 1.3 % | 1.3 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Flexural Strain, 2 mm/min; ISO 178 | |
| 1.8 % | 1.8 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| 1.7 % | 1.7 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 6.33 GPa | 918 ksi | 1 mm/min; ISO 527 |
| 6.63 GPa | 962 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 87.0 MPa | 12600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 87.0 MPa | 12600 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 5.92 GPa | 859 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 6.17 GPa | 895 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.310 J/cm @Temperature 23.0 °C |
0.581 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 1.47 J/cm @Temperature 23.0 °C |
2.75 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 9.00 kJ/m² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 43.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.9 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 41.4 µm/m-°C @Temperature -40.0 - 40.0 °C |
23.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 218 °C @Thickness 3.20 mm |
424 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 121 °C | 250 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 115 °C @Thickness 3.20 mm |
239 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |