Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 105.074 Agglomerated Sintered Molybdenum (Mo)
|
Particle Size |
88 µm |
88 µm |
98% less than |
H.C. Starck Amperit® 106.062 Sintered Molybdenum (Mo)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 515.074 Sintered Tungsten Carbide - Cobalt (WC-Co) 88-12
HS Number: 28499030 |
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 516.074 Tungsten Carbide - Cobalt (WC-Co) 88-12
HS Number: 28499030 |
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 518.001 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 526.062 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 526.074 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 582.072 Chromium Carbide-Nickel Chromium 80-20 (Cr3C2-NiCr)
|
Particle Size |
88 µm |
88 µm |
100% less than, Cr3C2 |
H.C. Starck Amperit® 585.3 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr)
Composition is of Cr3C2 only |
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 586.1 Chromium Carbide-Nickel Chromium 80-20 (Cr3C2-NiCr)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 705.1 Fused Chromium Oxide 96.0 % (Cr2O3)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 716.054 Chromium Oxide-Titanium Oxide-Silicon Oxide 92-3-5 (Cr2O3-TiO2-SiO2)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 740.3 Aluminum Oxide (Al2O3)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 744.3 Aluminum Oxide-Titanium Oxide 87-13 (Al2O3 - TiO2)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 782.3 Titanium Oxide (TiO2)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 553.065 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 554.071 Tungsten Carbide-Cobalt-Chromium 86-10-4 (WC-Co-Cr)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 599.074 Agglomerated Sintered Molybdenum Carbide (Cr2O3)
|
Particle Size |
88 µm |
88 µm |
Minimum of 90% less than |
H.C. Starck Amperit® 704.092 Chromium Oxide (Cr2O3) 99.5%
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 704.3 Chromium Oxide (Cr2O3) 99.5%
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 740.1 Aluminum Oxide (Al2O3)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 744.1 Aluminum Oxide-Titanium Oxide 87-13 (Al2O3 - TiO2)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 745.1 Aluminum Oxide-Titanium Oxide 60-40 (Al2O3-TiO2)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 782.1 Titanium Oxide (TiO2)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 584.1 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 516.1 Tungsten Carbide - Cobalt (WC-Co) 88-12
HS Number: 28499030 |
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 547.074 Tungsten Carbide-Nickel 88-12 (WC-Ni)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 551.074 Tungsten Carbide - Chromium Carbide - Nickel 70-20-7 (W-CrC-Ni)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 552.072 Tungsten Carbide - Chromium Carbide-Nickel 73-20-7 (WC-CrC-Ni)
|
Particle Size |
88 µm |
88 µm |
100% less than |
H.C. Starck Amperit® 584.054 Chromium Carbide-Nickel Chromium 75-25 (Cr3C2-NiCr)
|