Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 8.94 g/cc | 0.323 lb/in³ | |
Materion ToughMet® T3 AT120 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have e.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Materion ToughMet® T3 AT90 (OD≥4") ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have e.. |
|||
Density | 8.95 g/cc | 0.323 lb/in³ | |
Lucas-Milhaupt BRAZE 250 Silver Based Cadmium Free Filler Metal Characteristics:Braze 250 is an intermediate temperature silver brazing alloy with a long (325EF/180EC) melting range. It has a tendency to liquate (i.e. separate into low and high melting constitu.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Materion ToughMet® T3 CX90 ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have e.. |
|||
Density | 8.95 g/cc | 0.323 lb/in³ | |
Indium Corp. Indalloy 120 Tin-Lead Solder Alloy Information Provided by Indium Corporation |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Lucas-Milhaupt Silvaloy® 25 Brazing Alloy Silvaloy 25 is historically a modification of Silvaloy 30 with a further reduction in silver content resulting in a higher melting point and a longer melting range. Silvaloy 25 is used for brazing s.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 151 ZHC® COPPER, 3/4 Hard Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 151 ZHC® COPPER, Extra Hard Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 151 ZHC® COPPER, Hard Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 151 ZHC® COPPER, Spring Alloy C151 has excellent solderability, high conductivity, and good strength. C151 has superior high temperature softening resistance compared to pure copper C110.Applications can be found in high c.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 19210 XP-10 Copper Iron, 3/4 Hard 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 19210 XP-10 Copper Iron, Annealed 19210 has higher strengths than most copper alloys but thanks to its composition and processing it retains formability and conductivity that other copper alloys lose. Typical uses include cooling f.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 706 Copper Nickel 10%, Annealed 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 706 Copper Nickel 10%, Hard 706 exhibits excellent corrosion resistance, especially in marine applications. It has a relatively high strength and has resistance at elevated temperatures. The cost is relatively high compared to.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 715 Copper Nickel 30%, Annealed 715 exhibits excellent corrosion resistance, especially in marine applications. It has moderately high strength and has good creep resistance at elevated temperatures. The cost is relatively high co.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 101 OFE COPPER (Certified), 1/2 Hard Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 101 OFE COPPER (Certified), 3/4 Hard Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 101 OFE COPPER (Certified), Extra Hard Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 101 OFE COPPER (Certified), Extra Spring Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 101 OFE COPPER (Certified), Spring Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 102 OF COPPER (Non-Certified), 1/2 Hard Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 102 OF COPPER (Non-Certified), 1/4 Hard Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 102 OF COPPER (Non-Certified), 3/4 Hard Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 102 OF COPPER (Non-Certified), Extra Spring Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 102 OF COPPER (Non-Certified), Spring Alloy 102 is an oxygen-free copper which has better forming, resistance to hydrogen embrittlement, and brazing characteristics than C110 ETP. C102 has good solder-ability and corrosion resistance an.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | Annealed |
Eagle Brass 101 OFE COPPER (Certified), 1/4 Hard Alloy 101 is known as Oxygen-Free Electronic (OFE). It reaches a minimum of 101% IACS conductivity rating. It is the most expensive out of the 101- 110 group because of its higher purity.Information.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Carlson 70 30 Cu Ni Copper-Nickel Alloy General DescriptionCarlson alloy 70 30 Cu Ni is a copper nickel alloy with excellent resistance to corrosion and erosion. It is strong and ductile. 70 30 Cu Ni is utilized in areas where high temp.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
ATI Allvac® Nickelvac® C-276 UNS N10276 Nickel Superalloy Uses: Pressure vessels, pumps, valves, HX tubing and piping for the CPI and HPI. Trays, flanges, fasteners, wire, screens.Property values are for samples in the metallurgical condition: 2050°F anne.. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
ATI Allvac® Nickelvac® HC-276 Nickel Superalloy, Heat Treatment: 1121°C (2050°F) Anneal Data provided by Allvac.Applications: High temperature applications also requiring good resistance to corrosive fluids, such as liquids and combustion products. |
|||
Density | 8.94 g/cc | 0.323 lb/in³ | |
Materion ToughMet® T3 CX105 (OD ToughMet® is Brush Wellman's solution for severe service material problems. By applying their EquaCast® process, tailored alloying additions and spinodal hardening technology, they have engin.. |