DuPont Performance Polymers Zytel® HTN 52G35HSL NC010 Polyphthalamide (PPA)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 40% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF DuPont Performance Polymers Zytel® HTN 52G35HSL NC010 Polyphthalamide (PPA).pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Zytel® HTN52G35HSL NC010 is a 35% glass reinforced, heat stabilized, lubricated high performance polyamide resin that can be molded in water heated molds.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.47 g/cc
1.47 g/cc
DAM; ASTM D792
Density 1.45 g/cc
0.0524 lb/in³
DAM; ISO 1183
Filler Content 35 %
35 %
DAM
Linear Mold Shrinkage 0.0025 cm/cm
<br>@Thickness 1.60 mm
 0.0025 in/in
<br>@Thickness 0.0630 in
 Flow; DAM
0.0030 cm/cm
<br>@Thickness 3.20 mm
 0.0030 in/in
<br>@Thickness 0.126 in
 Flow; DAM
0.010 cm/cm
<br>@Thickness 1.60 mm
 0.010 in/in
<br>@Thickness 0.0630 in
 Transverse; DAM
0.010 cm/cm
<br>@Thickness 3.20 mm
 0.010 in/in
<br>@Thickness 0.126 in
 Transverse; DAM
Linear Mold Shrinkage, Flow 0.0020 cm/cm
<br>@Thickness 2.00 mm
 0.0020 in/in
<br>@Thickness 0.0787 in
 DAM; ISO 294-4
Mechanical Properties Metric English Comments
Hardness, Rockwell M 105
105
DAM; ASTM D785
Hardness, Rockwell R 124
124
DAM; ASTM D785
Tensile Strength at Break 180 MPa
<br>@Temperature 23.0 °C
 26100 psi
<br>@Temperature 73.4 °F
 50%RH; ISO 527
200 MPa
<br>@Temperature 23.0 °C
 29000 psi
<br>@Temperature 73.4 °F
 DAM; ISO 527
Tensile Strength 72.4 MPa
<br>@Temperature 200 °C
 10500 psi
<br>@Temperature 392 °F
 DAM; ASTM D638
80.0 MPa
<br>@Temperature 175 °C
 11600 psi
<br>@Temperature 347 °F
 DAM; ASTM D638
89.0 MPa
<br>@Temperature 150 °C
 12900 psi
<br>@Temperature 302 °F
 DAM; ASTM D638
124 MPa
<br>@Temperature 100 °C
 18000 psi
<br>@Temperature 212 °F
 DAM; ASTM D638
168 MPa
<br>@Temperature 23.0 °C
 24400 psi
<br>@Temperature 73.4 °F
 50%RH; ASTM D638
188 MPa
<br>@Temperature 60.0 °C
 27300 psi
<br>@Temperature 140 °F
 DAM; ASTM D638
204 MPa
<br>@Temperature 23.0 °C
 29600 psi
<br>@Temperature 73.4 °F
 DAM; ASTM D638
230 MPa
<br>@Temperature -40.0 °C
 33400 psi
<br>@Temperature -40.0 °F
 DAM; ASTM D638
Tensile Stress 21.57 MPa
<br>@Strain 0.210 %,<br> Temperature 23.0 °C
 3128 psi
<br>@Strain 0.210 %,<br> Temperature 73.4 °F
 DAM; ISO 11403-1/-2
23.46 MPa
<br>@Strain 0.510 %,<br> Temperature 150 °C
 3403 psi
<br>@Strain 0.510 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1/-2
24.31 MPa
<br>@Strain 0.210 %,<br> Temperature 0.000 °C
 3526 psi
<br>@Strain 0.210 %,<br> Temperature 32.0 °F
 DAM; ISO 11403-1/-2
24.56 MPa
<br>@Strain 0.220 %,<br> Temperature 40.0 °C
 3562 psi
<br>@Strain 0.220 %,<br> Temperature 104 °F
 DAM; ISO 11403-1/-2
24.63 MPa
<br>@Strain 0.200 %,<br> Temperature -20.0 °C
 3572 psi
<br>@Strain 0.200 %,<br> Temperature -4.00 °F
 DAM; ISO 11403-1/-2
25.85 MPa
<br>@Strain 0.210 %,<br> Temperature -20.0 °C
 3749 psi
<br>@Strain 0.210 %,<br> Temperature -4.00 °F
 50%RH; ISO 11403-1/-2
26.02 MPa
<br>@Strain 0.510 %,<br> Temperature 120 °C
 3774 psi
<br>@Strain 0.510 %,<br> Temperature 248 °F
 50%RH; ISO 11403-1/-2
26.87 MPa
<br>@Strain 0.230 %,<br> Temperature 0.000 °C
 3897 psi
<br>@Strain 0.230 %,<br> Temperature 32.0 °F
 50%RH; ISO 11403-1/-2
27.0 MPa
<br>@Strain 0.520 %,<br> Temperature 150 °C
 3920 psi
<br>@Strain 0.520 %,<br> Temperature 302 °F
 DAM; ISO 11403-1/-2
29.31 MPa
<br>@Strain 0.270 %,<br> Temperature 60.0 °C
 4251 psi
<br>@Strain 0.270 %,<br> Temperature 140 °F
 DAM; ISO 11403-1/-2
29.53 MPa
<br>@Strain 0.260 %,<br> Temperature 23.0 °C
 4283 psi
<br>@Strain 0.260 %,<br> Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
30.36 MPa
<br>@Strain 0.520 %,<br> Temperature 90.0 °C
 4403 psi
<br>@Strain 0.520 %,<br> Temperature 194 °F
 50%RH; ISO 11403-1/-2
31.33 MPa
<br>@Strain 0.480 %,<br> Temperature 120 °C
 4544 psi
<br>@Strain 0.480 %,<br> Temperature 248 °F
 DAM; ISO 11403-1/-2
33.66 MPa
<br>@Strain 0.430 %,<br> Temperature 90.0 °C
 4882 psi
<br>@Strain 0.430 %,<br> Temperature 194 °F
 DAM; ISO 11403-1/-2
33.8 MPa
<br>@Strain 0.480 %,<br> Temperature 60.0 °C
 4900 psi
<br>@Strain 0.480 %,<br> Temperature 140 °F
 50%RH; ISO 11403-1/-2
33.82 MPa
<br>@Strain 0.370 %,<br> Temperature 40.0 °C
 4905 psi
<br>@Strain 0.370 %,<br> Temperature 104 °F
 50%RH; ISO 11403-1/-2
40.0 MPa
<br>@Strain 1.01 %,<br> Temperature 150 °C
 5800 psi
<br>@Strain 1.01 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1/-2
44.91 MPa
<br>@Strain 1.02 %,<br> Temperature 120 °C
 6514 psi
<br>@Strain 1.02 %,<br> Temperature 248 °F
 50%RH; ISO 11403-1/-2
45.14 MPa
<br>@Strain 0.400 %,<br> Temperature 23.0 °C
 6547 psi
<br>@Strain 0.400 %,<br> Temperature 73.4 °F
 DAM; ISO 11403-1/-2
46.55 MPa
<br>@Strain 1.03 %,<br> Temperature 150 °C
 6752 psi
<br>@Strain 1.03 %,<br> Temperature 302 °F
 DAM; ISO 11403-1/-2
47.58 MPa
<br>@Strain 0.400 %,<br> Temperature 0.000 °C
 6901 psi
<br>@Strain 0.400 %,<br> Temperature 32.0 °F
 DAM; ISO 11403-1/-2
48.33 MPa
<br>@Strain 0.420 %,<br> Temperature 40.0 °C
 7010 psi
<br>@Strain 0.420 %,<br> Temperature 104 °F
 DAM; ISO 11403-1/-2
48.71 MPa
<br>@Strain 0.400 %,<br> Temperature -20.0 °C
 7065 psi
<br>@Strain 0.400 %,<br> Temperature -4.00 °F
 DAM; ISO 11403-1/-2
51.27 MPa
<br>@Strain 1.52 %,<br> Temperature 150 °C
 7436 psi
<br>@Strain 1.52 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1/-2
52.09 MPa
<br>@Strain 1.02 %,<br> Temperature 90.0 °C
 7555 psi
<br>@Strain 1.02 %,<br> Temperature 194 °F
 50%RH; ISO 11403-1/-2
52.74 MPa
<br>@Strain 0.430 %,<br> Temperature -20.0 °C
 7649 psi
<br>@Strain 0.430 %,<br> Temperature -4.00 °F
 50%RH; ISO 11403-1/-2
52.86 MPa
<br>@Strain 0.440 %,<br> Temperature 0.000 °C
 7667 psi
<br>@Strain 0.440 %,<br> Temperature 32.0 °F
 50%RH; ISO 11403-1/-2
56.27 MPa
<br>@Strain 0.970 %,<br> Temperature 120 °C
 8161 psi
<br>@Strain 0.970 %,<br> Temperature 248 °F
 DAM; ISO 11403-1/-2
57.13 MPa
<br>@Strain 0.520 %,<br> Temperature 60.0 °C
 8286 psi
<br>@Strain 0.520 %,<br> Temperature 140 °F
 DAM; ISO 11403-1/-2
57.71 MPa
<br>@Strain 1.50 %,<br> Temperature 120 °C
 8370 psi
<br>@Strain 1.50 %,<br> Temperature 248 °F
 50%RH; ISO 11403-1/-2
58.76 MPa
<br>@Strain 0.510 %,<br> Temperature 23.0 °C
 8522 psi
<br>@Strain 0.510 %,<br> Temperature 73.4 °F
 50%RH; ISO 11403-1/-2
59.16 MPa
<br>@Strain 2.00 %,<br> Temperature 150 °C
 8580 psi
<br>@Strain 2.00 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1/-2
59.45 MPa
<br>@Strain 0.940 %,<br> Temperature 60.0 °C
 8623 psi
<br>@Strain 0.940 %,<br> Temperature 140 °F
 50%RH; ISO 11403-1/-2
60.05 MPa
<br>@Strain 1.54 %,<br> Temperature 150 °C
 8710 psi
<br>@Strain 1.54 %,<br> Temperature 302 °F
 DAM; ISO 11403-1/-2
60.37 MPa
<br>@Strain 0.840 %,<br> Temperature 90.0 °C
 8756 psi
<br>@Strain 0.840 %,<br> Temperature 194 °F
 DAM; ISO 11403-1/-2
63.4 MPa
<br>@Strain 0.730 %,<br> Temperature 40.0 °C
 9200 psi
<br>@Strain 0.730 %,<br> Temperature 104 °F
 50%RH; ISO 11403-1/-2
65.23 MPa
<br>@Strain 2.50 %,<br> Temperature 150 °C
 9461 psi
<br>@Strain 2.50 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1/-2
67.45 MPa
<br>@Strain 2.01 %,<br> Temperature 120 °C
 9783 psi
<br>@Strain 2.01 %,<br> Temperature 248 °F
 50%RH; ISO 11403-1/-2
67.85 MPa
<br>@Strain 1.54 %,<br> Temperature 90.0 °C
 9841 psi
<br>@Strain 1.54 %,<br> Temperature 194 °F
 50%RH; ISO 11403-1/-2
69.31 MPa
<br>@Strain 0.600 %,<br> Temperature 23.0 °C
 10050 psi
<br>@Strain 0.600 %,<br> Temperature 73.4 °F
 DAM; ISO 11403-1/-2
69.59 MPa
<br>@Strain 3.01 %,<br> Temperature 150 °C
 10090 psi
<br>@Strain 3.01 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1/-2
69.78 MPa
<br>@Strain 2.05 %,<br> Temperature 150 °C
 10120 psi
<br>@Strain 2.05 %,<br> Temperature 302 °F
 DAM; ISO 11403-1/-2
71.76 MPa
<br>@Strain 0.600 %,<br> Temperature 0.000 °C
 10410 psi
<br>@Strain 0.600 %,<br> Temperature 32.0 °F
 DAM; ISO 11403-1/-2
72.71 MPa
<br>@Strain 3.51 %,<br> Temperature 150 °C
 10550 psi
<br>@Strain 3.51 %,<br> Temperature 302 °F
 50%RH; ISO 11403-1/-2
72.74 MPa
<br>@Strain 0.640 %,<br> Temperature 40.0 °C
 10550 psi
<br>@Strain 0.640 %,<br> Temperature 104 °F
 DAM; ISO 11403-1/-2