Wellman Wellpet® GF100-N1 30% Glass Fiber Reinforced, Natural PET
| Category | Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellpet® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellpet® GF100-N1 30% Glass Fiber Reinforced, Natural PET.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Glass Fiber Reinforced, Natural PETInformation provided by Wellman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ISO 1183-87 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in | ISO DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ISO DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527-93 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-93 |
| Flexural Strength | 190 MPa | 27600 psi | ISO 178-93 |
| Flexural Modulus | 9.80 GPa | 1420 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 250 °C | 482 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 220 °C | 428 °F | ISO 75-93 |
Users viewing this material also viewed the following:
- Palm Labs Adhesives TURBO FUSE SERIES 190-HT (4000 cp HIGH TEMPERATURE) Rapid Bonding Adhesive
- ExxonMobil LL 8450 Rotational Molding Resin (discontinued **)
- LNP ULTEM® EXCP0096 Polyetherimide, 30% Carbon Fiber Reinforcement, 10% PTFE Lubricant (discontinued **)
- Lehmann & Voss LUVOCOM® 21-7979 Polyamide 6/6T, with glass fiber, 8-mm-granulate
- Karina 800-21/9-IS-RG Coke PVC Compound
- Momentive Performance Materials TSE3941 White Adhesive Sealant, Fast Cure Paste
- LyondellBasell Hostacomâ„¢ 62F4-2C Polypropylene Homopolymer
- Techmer ES HiFill® PBT E
- Borealis HG385MO Polypropylene
- Dow Corning 9011 Silicone Elastomer Blend
Copyright © lookpolymers.com All Rights Reserved