PolyOne Edgetek® SF-45GF/000 Polyphenylene Sulfide (PPS), Glass Filled (discontinued **)
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® SF-45GF/000 Polyphenylene Sulfide (PPS), Glass Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Fiber ReinforcedUL 94 V0PolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.70 g/cc | 1.70 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength, Ultimate | 169 MPa | 24500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 15.2 GPa | 2200 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 241 MPa | 35000 psi | ASTM D790 |
| Flexural Modulus | 15.2 GPa | 2200 ksi | ASTM D790 |
| Compressive Strength | 179 MPa | 26000 psi | ASTM D695 |
| Izod Impact, Notched | 0.908 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 25.2 µm/m-°C @Temperature 20.0 °C |
14.0 µin/in-°F @Temperature 68.0 °F |
ASTM D696 |
| Thermal Conductivity | >= 0.432 W/m-K | >= 3.00 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 282 °C | 540 °F | Annealed, 0.125 in bars; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 266 °C | 510 °F | Annealed, 0.125 in bars; ASTM D648 |
| Flammability, UL94 | V-0 | V-0 | All Colors; 0.028 in.; PolyOne Internal |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 316 °C | 600 °F | Molding |
| Mold Temperature | >= 121 °C | >= 250 °F | |
| Drying Temperature | 121 °C | 250 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® ML3729 PC
- Momentive Performance Materials "PG" Pyrolytic Graphite
- Haynes 214® alloy, 10% cold reduction, 980°C (1800°F) for 5 minutes
- Techmer ES Electrafil® J-50/CF/10/TF/13/SI/2 Polycarbonate, 10% Carbon Fiber Reinforced, 13% PTFE, 2% Silicone
- Universal Wire Works Greek Ascoloy (AMS 5817) Filler Metal
- Zeon Chemicals Nipol® 1022x59 Nitrile Elastomer
- A. Schulman FORMION™ FI 397 Ionomer
- C.O.I.M. FILCO® 362 Film Former for Glass Fiber Sizes
- Zircar Zirconia ZYF-150 Zirconia Felt Insulation
Copyright © lookpolymers.com All Rights Reserved