- Wellman Wellamid® FRGF25-66 NBK3 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant
Wellman Wellamid® FRGF25-66 NBK3 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Wellman Engineering Resins |
| Trade Name | Wellamid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Wellman Wellamid® FRGF25-66 NBK3 Nylon 66, 25% Glass Fiber Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
All information provided by Wellman Engineered Resins.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.48 g/cc | 0.0535 lb/in³ | ISO 1183-87 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0070 cm/cm | 0.0030 - 0.0070 in/in | DIS 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.012 cm/cm | 0.0080 - 0.012 in/in | DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 115 MPa | 16700 psi | ISO 527-93 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-93 |
| Flexural Strength | 165 MPa | 23900 psi | ISO 178-93 |
| Flexural Modulus | 7.10 GPa | 1030 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-93 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
Users viewing this material also viewed the following:
- NeXolve Clear Optionox® Polyimide Film/Coating
- NOVA Chemicals EPS M77BHD Expandable Polystyrene Resin
- Polykemi AB POLYfill PPH GF2030 PD2 Polypropylene Homopolymer, Glass Fibre-Reinforced, Chemically Coupled
- Multibase Multi-Flex® 1047 Black TPO Thermoplastic Polyolefin Elastomer
- Hexcel® Redux® 208/4-NA Foaming adhesive film
- Eurostar Staramide AG7H PA66, 35% Glass Filled, Injection Molded
- Beijing Ranger Chem B-63 Liquid Epoxy Resin
- Abatron AboCast 8103-20 High-Performance Dielectric Epoxy
- Arlon 44580R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
- H.C. Starck Amperit® 529.074 Tungsten Carbide - Hastalloy C 85-15 (NiMoCrFeCo)
Copyright © lookpolymers.com All Rights Reserved