Vyncolit X640 Resole Phenolic
| Category | Polymer , Thermoset , Filled/Reinforced Thermoset , Phenolic , Phenolic, Resole, Glass Fiber Filled |
| Manufacturer | Vyncolit N.V., Sumitomo Bakelite |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Vyncolit X640 Resole Phenolic.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber filled phenolic molding compound with excellent mechanical and thermal properties.USES: Information provided by Vyncolit, a Sumitomo Bak Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.650 g/cc | 0.0235 lb/in³ | Powder Density; ISO 60 |
| Density | 1.70 g/cc | 0.0614 lb/in³ | Relative Density; ISO 1183 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | Injection Molding; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 125 MPa | 18100 psi | ISO 527 |
| Elongation at Break | 0.80 % | 0.80 % | Tensile; ISO 527 |
| 1.5 % | 1.5 % | Flexure; ISO 178 | |
| Tensile Modulus | 20.0 GPa | 2900 ksi | ISO 527 |
| Flexural Strength | 240 MPa | 34800 psi | At Rupture; ISO 178 |
| Flexural Modulus | 17.0 GPa | 2470 ksi | ISO 178 |
| Compressive Strength | 275 MPa | 39900 psi | ISO 604 |
| Charpy Impact Unnotched | 1.80 J/cm² | 8.57 ft-lb/in² | ISO 179 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature 20.0 °C |
13.9 µin/in-°F @Temperature 68.0 °F |
TMA |
| CTE, linear, Transverse to Flow | 45.0 µm/m-°C @Temperature 20.0 °C |
25.0 µin/in-°F @Temperature 68.0 °F |
TMA |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 Af |
| Flammability, UL94 | V-1 @Thickness 1.60 mm |
V-1 @Thickness 0.0630 in |
|
| V-0 @Thickness 4.00 mm |
V-0 @Thickness 0.157 in |
||
| Shrinkage | 0.25 % | 0.25 % | Post Shrinkage; ISO 2577 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 243 |
| Comparative Tracking Index | 125 V | 125 V | IEC 112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| ISO type | PF 1 C1 | |
| Main Filler | Glass Fiber | |
| Molding Method | Compression, transfer, injection |
Users viewing this material also viewed the following:
- Resin Technology Group 405 Oxy-Bond™ Electrically Conductive Epoxy Adhesive
- Intercontinental Polymers 554 PBT Polymer Type - Elastomer Polyester Pellets
- Westlake Plastics Zelux® 40% GF Polycarbonate 40% Glass Filled
- Hippe EP GC 204 Woven Glass Cloth Reinforced Epoxy Resin - Sheet
- Arkema Group Rilsan® AUM 50 NOIR T6LD Nylon 12, 50% Glass Bead Filled (Dry)
- Azoty Tarnow™ Tarnamid® T-27 CF20 Polyamide 6 20% Carbon Fiber- Antistatic and Electroconductive
- BASF Ultramid® 8202C HS BK-102 PA6 (Dry)
- 3M Scotch-Weld™ DP608 Structural Adhesive
- KKPC KOSYN KSL 106 Styrene-Butadiene Latex
Copyright © lookpolymers.com All Rights Reserved