Vyncolit Neopreg Kinel® SK60 L8G Glass Fiber Reinforced Molding Compound

Category Polymer , Thermoset , Epoxy , Epoxy Molding Compound , Filled/Reinforced Thermoset
Manufacturer Vyncolit N.V., Sumitomo Bakelite
Trade Name Neopreg Kinel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Vyncolit Neopreg Kinel® SK60 L8G Glass Fiber Reinforced Molding Compound.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High flow, epoxy based molding compound long glass fiber reinforced with excellent long term property retention over a wide temperature range and climate conditions. It is particularly suited for over molding.Information provided by Sumitomo Bak North America, Inc.
Physical Properties Metric English Comments
Bulk Density 0.500 g/cc
0.0181 lb/in³
ISO 60
Density 1.80 g/cc
0.0650 lb/in³
ISO 1183
Water Absorption 0.060 %
0.060 %
ISO 62
Linear Mold Shrinkage 0.0014 cm/cm
0.0014 in/in
ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 96.0 MPa
13900 psi
ISO 527-1
Elongation at Break 0.60 %
0.60 %
ISO 527-1
Tensile Modulus 17.0 GPa
2470 ksi
ISO 527-1
Flexural Strength 204 MPa
29600 psi
ISO 178
Flexural Modulus 15.0 GPa
2180 ksi
ISO 178
Compressive Strength 232 MPa
33600 psi
ISO 604
Charpy Impact, Notched 4.60 J/cm²
21.9 ft-lb/in²
ISO 179-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 5.70 µm/m-°C
3.17 µin/in-°F
TMA
CTE, linear, Transverse to Flow 69.0 µm/m-°C
38.3 µin/in-°F
TMA
Glass Transition Temp, Tg 165 °C
329 °F
Electrical Properties Metric English Comments
Dielectric Strength 28.0 kV/mm
711 kV/in
IEC 60243-1
Comparative Tracking Index 600 V
600 V
IEC 60250
Descriptive Properties Value Comments
Color Dark Grey
Molding Method Compression
Injection
Transfer