H.C. Starck Pure Molybdenum, Sheet Premium Grade PS-100-2

Category Metal , Nonferrous Metal , Molybdenum Alloy , Refractory Metal , Pure Element
Manufacturer H.C. Starck
Trade Name
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF H.C. Starck Pure Molybdenum, Sheet Premium Grade PS-100-2.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
Description of Product: Rolled molybdenum sheet produced from pressed and sintered powder metallurgy sheet bar.Structure: Sheet will be supplied in a stress-relieved condition unless otherwise requested.Information provided by H.C. Starck.
Mechanical Properties Metric English Comments
Tensile Strength >= 689 MPa
<br>@Thickness 1.52 - 2.54 mm
 >= 100000 psi
<br>@Thickness 0.0600 - 0.100 in
 ASTM E-8
>= 689 MPa
<br>@Thickness 2.54 - 4.75 mm
 >= 100000 psi
<br>@Thickness 0.100 - 0.187 in
 ASTM E-8
>= 724 MPa
<br>@Thickness 0.508 - 1.52 mm
 >= 105000 psi
<br>@Thickness 0.0200 - 0.0600 in
 ASTM E-8
>= 758 MPa
<br>@Thickness 0.127 - 0.254 mm
 >= 110000 psi
<br>@Thickness 0.00500 - 0.0100 in
 ASTM E-8
>= 758 MPa
<br>@Thickness 0.254 - 0.508 mm
 >= 110000 psi
<br>@Thickness 0.0100 - 0.0200 in
 ASTM E-8
Tensile Strength, Yield >= 552 MPa
<br>@Strain 0.200 %,<br> Thickness 1.52 - 2.54 mm
 >= 80000 psi
<br>@Strain 0.200 %,<br> Thickness 0.0600 - 0.100 in
 ASTM E-8
>= 552 MPa
<br>@Strain 0.200 %,<br> Thickness 2.54 - 4.75 mm
 >= 80000 psi
<br>@Strain 0.200 %,<br> Thickness 0.100 - 0.187 in
 ASTM E-8
>= 621 MPa
<br>@Strain 0.200 %,<br> Thickness 0.127 - 0.254 mm
 >= 90000 psi
<br>@Strain 0.200 %,<br> Thickness 0.00500 - 0.0100 in
 ASTM E-8
>= 621 MPa
<br>@Strain 0.200 %,<br> Thickness 0.254 - 0.508 mm
 >= 90000 psi
<br>@Strain 0.200 %,<br> Thickness 0.0100 - 0.0200 in
 ASTM E-8
>= 662 MPa
<br>@Strain 0.200 %,<br> Thickness 0.508 - 1.52 mm
 >= 96000 psi
<br>@Strain 0.200 %,<br> Thickness 0.0200 - 0.0600 in
 ASTM E-8
Elongation at Break >= 5.0 %
<br>@Thickness 0.127 - 0.254 mm
 >= 5.0 %
<br>@Thickness 0.00500 - 0.0100 in
 ASTM E-8
>= 6.0 %
<br>@Thickness 0.254 - 0.508 mm
 >= 6.0 %
<br>@Thickness 0.0100 - 0.0200 in
 ASTM E-8
>= 10 %
<br>@Thickness 0.508 - 1.52 mm
 >= 10 %
<br>@Thickness 0.0200 - 0.0600 in
 ASTM E-8
>= 14 %
<br>@Thickness 1.52 - 2.54 mm
 >= 14 %
<br>@Thickness 0.0600 - 0.100 in
 ASTM E-8
>= 18 %
<br>@Thickness 2.54 - 4.75 mm
 >= 18 %
<br>@Thickness 0.100 - 0.187 in
 ASTM E-8
Bend Radius, Minimum 1.0 t
<br>@Thickness <=3.17 mm
 1.0 t
<br>@Thickness <=0.125 in
 Bend Severity 90°, specimens at least 1&quot; by 2&quot;, transverse direction
1.0 t
<br>@Thickness <=1.02 mm
 1.0 t
<br>@Thickness <=0.0400 in
 Bend Severity 180°, specimens at least 1&quot; by 2&quot;, transverse direction
2.0 t
<br>@Thickness <=4.75 mm
 2.0 t
<br>@Thickness <=0.187 in
 Bend Severity 90°, specimens at least 1&quot; by 2&quot;, transverse direction
2.0 t
<br>@Thickness <=2.03 mm
 2.0 t
<br>@Thickness <=0.0800 in
 Bend Severity 180°, specimens at least 1&quot; by 2&quot;, transverse direction
Component Elements Properties Metric English Comments
Aluminum, Al <= 0.0020 %
<= 0.0020 %
Calcium, Ca <= 0.0030 %
<= 0.0030 %
Carbon, C <= 0.0050 %
<= 0.0050 %
Chromium, Cr <= 0.0050 %
<= 0.0050 %
Copper, Cu <= 0.0020 %
<= 0.0020 %
Iron, Fe <= 0.0050 %
<= 0.0050 %
Lead, Pb <= 0.0020 %
<= 0.0020 %
Magnesium, Mg <= 0.0010 %
<= 0.0010 %
Manganese, Mn <= 0.0010 %
<= 0.0010 %
Molybdenum, Mo >= 99.95 %
>= 99.95 %
by difference
Nickel, Ni <= 0.0020 %
<= 0.0020 %
Silicon, Si <= 0.0030 %
<= 0.0030 %
Tin, Sn <= 0.0030 %
<= 0.0030 %
Titanium, Ti <= 0.0020 %
<= 0.0020 %
Descriptive Properties Value Comments
Olsen Cup Test >0.225 in. cup depth
Sheet thickness 0.015 in.
>0.26 in. cup depth
Sheet thickness 0.030 in.
>0.28 in. cup depth
Sheet thickness 0.040 in.
>0.305 in. cup depth
Sheet thickness 0.050 in.
>0.33 in. cup depth
Sheet thickness 0.060 in.