NIZHNEKAMSKNEFTEKHIM PE 5118Q (18603) Linear Low Density Polyethylene
| Category | Polymer , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | NIZHNEKAMSKNEFTEKHIM Inc |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | NIZHNEKAMSKNEFTEKHIM PE 5118Q (18603) Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product obtained by gas phase polymerization of ethylene in presence of complex metalorganic catalysts.Information provided by manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.916 - 0.920 g/cc | 0.0331 - 0.0332 lb/in³ | Base Resin; ASTM D1505 |
| Melt Flow | 2.8 - 3.4 g/10 min @Load 2.16 kg, Temperature 190 °C |
2.8 - 3.4 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1283/L |
| 84 - 102 g/10 min @Load 21.6 kg, Temperature 190 °C |
84 - 102 g/10 min @Load 47.6 lb, Temperature 374 °F |
Flow@21.6kg/Flow@2.16kg ratio < 30; ASTM D1283 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | >= 53.0 MPa | >= 7690 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | >= 30.0 MPa | >= 4350 psi | ASTM D882 |
| Film Elongation at Break, MD | >= 500 % | >= 500 % | ASTM D882 |
| Film Elongation at Break, TD | >= 900 % | >= 900 % | ASTM D882 |
| Tensile Modulus | >= 0.115 GPa | >= 16.7 ksi | 2% sec, MD; ASTM D882 |
| >= 0.120 GPa | >= 17.4 ksi | 2% sec, TD; ASTM D882 | |
| Elmendorf Tear Strength, MD | >= 7.48 g/micron | >= 190 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | >= 17.7 g/micron | >= 450 g/mil | ASTM D1922 |
| Dart Drop Test | >= 100 g | >= 0.221 lb | ASTM D1709 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Gel Content (pcs./m²) | 0 | > 1mm |
| 245 | (0.2-0.5)mm | |
| 250 | > 0.2mm (totally) | |
| 5 | (0.5-1.0)mm |
Users viewing this material also viewed the following:
- Plaskolite Optix® CA - 75 UVA General Purpose Acrylic Resin
- PolyOne Trilliant™ HC HC0200-5001 XR Grey Thermoplastic Elastomer (TPE)
- PolyOne Geon™ Vinyl Flexible C6501 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Overview of materials for Polyphenylene Sulfide (PPS) with 40% Carbon Fiber Filler
- Karina E 42/261-GEN Dark Red MBATCH (SP31543) for PVC
- A. Schulman POLYFORT™ FPP 1902HU Talc Fortified Polypropylene
- Chosun Refractories CTL-Z2 Monolithic Refractories for Ladle and Tundish
- Bulk Molding Compounds tetra-DUR L 4305 Bulk Molding Compound
- 3M 760 Hybrid Adhesive Sealant
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N330 Filler
Copyright © lookpolymers.com All Rights Reserved