Total PPH 4026 Polypropylene Homopolymer, Sheet Extrusion and Thermoforming

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Sheet/Thermoforming Grade
Manufacturer	Total Atofina
Trade Name	PPH
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPH 4026 Polypropylene Homopolymer, Sheet Extrusion and Thermoforming.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

This grade belongs to the Total Ecosolution line.Polypropylene PPH 4026 is a polypropylene homopolymer specifically developed to offer outstanding processability for sheet extrusion and thermoforming applications.Polypropylene PPH 4026 is characterized by a higher stiffness than conventional nucleated homopolymers, a good impact resistance and an excellent clarity. Polypropylene PPH 4026 allows for wall thickness reduction while maintaining appropriate top load and crush resistances.Polypropylene PPH 4026 has excellent organoleptic properties making it suitable for the most sensitive packaging application.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.905 g/cc	0.905 g/cc	ISO 1183
Bulk Density	0.525 g/cc	0.0190 lb/in³	ISO 1183
Melt Flow	3.0 g/10 min @Load 2.16 kg, Temperature 230 °C	3.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	95	95	ISO 2039-2
Tensile Strength, Yield	39.0 MPa	5660 psi	ISO 527-2
Elongation at Yield	9.0 %	9.0 %	ISO 527-2
Tensile Modulus	2.05 GPa	297 ksi	ISO 527-2
Flexural Modulus	2.00 GPa	290 ksi	ISO 178
Izod Impact, Notched (ISO)	5.00 kJ/m²	2.38 ft-lb/in²	ISO 180
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
Melting Point	163 °C	325 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	110 °C	230 °F	120°C per hour; ISO 752
Deflection Temperature at 1.8 MPa (264 psi)	60.0 °C	140 °F	120°C per hour; ISO 752
Vicat Softening Point	97.0 °C @Load 5.10 kg	207 °F @Load 11.2 lb	50°C per hour; ISO 306
	153 °C @Load 1.02 kg	307 °F @Load 2.25 lb	50°C per hour; ISO 306