Unitika EX-1030 PA6, Dry

Category	Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer	Unitika
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Unitika EX-1030 PA6, Dry.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

High-impact nylonInformation provided by Unitika Ltd.

Physical Properties	Metric	English	Comments
Density	1.04 g/cc	0.0376 lb/in³	ISO 1183
Water Absorption	1.3 % @Time 86400 sec	1.3 % @Time 24.0 hour	ISO 62
Moisture Absorption at Equilibrium	2.0 %	2.0 %	50% RH; ISO 62
Linear Mold Shrinkage, Flow	0.012 cm/cm @Thickness 3.20 mm	0.012 in/in @Thickness 0.126 in
Linear Mold Shrinkage, Transverse	0.016 cm/cm @Thickness 3.20 mm	0.016 in/in @Thickness 0.126 in

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	93	93	ISO 2039
Tensile Strength, Yield	39.0 MPa	5660 psi	ISO 527-1/-2
Elongation at Break	>= 200 %	>= 200 %	ISO 527-1/-2
Elongation at Yield	5.0 %	5.0 %	ISO 527-1/-2
Tensile Modulus	1.50 GPa	218 ksi	ISO 527-1/-2
Flexural Strength	53.0 MPa	7690 psi	ISO 178
Flexural Modulus	1.50 GPa	218 ksi	ISO 178
Charpy Impact Unnotched	NB	NB	ISO 179-1
Charpy Impact, Notched	9.10 J/cm²	43.3 ft-lb/in²	ISO 179-1

Thermal Properties	Metric	English	Comments
CTE, linear	120 µm/m-°C	66.7 µin/in-°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	82.0 °C	180 °F	ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	47.0 °C	117 °F	ISO 75-1/-2

Electrical Properties	Metric	English	Comments
Volume Resistivity	3.00e+13 ohm-cm	3.00e+13 ohm-cm	IEC 60093
Dielectric Constant	2.9 @Frequency 1.00e+6 Hz	2.9 @Frequency 1.00e+6 Hz	IEC 60250
Dielectric Strength	42.1 kV/mm @Thickness 1.00 mm	1070 kV/in @Thickness 0.0394 in	IEC 60243-1
Dissipation Factor	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	IEC 60250