BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® 8233G HS 33% Glass Filled PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced nylon 6 molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also available in non-heat stabilized and/or pigmented versions.
Physical Properties Metric English Comments
Density 1.136 g/cc
0.04104 lb/in³
Melt; ISO 1183
1.39 g/cc
0.0502 lb/in³
ISO 1183
Water Absorption 1.1 %
1.1 %
24 hour; ISO Test
6.4 %
6.4 %
ISO 62
Moisture Absorption at Equilibrium 1.8 %
1.8 %
23°C/50% R.H.; ISO 62
Relative Viscosity 2.6 cP
2.6 cP
ISO Test; 96 % SAV
Viscosity Measurement 50
50
Formic Acid
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
ASTM Data; MD
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM Test
Tensile Strength at Break 195 MPa
28300 psi
0.2 in/min; ASTM Test
83.0 MPa

@Temperature 120 °C
12000 psi

@Temperature 248 °F
ASTM Test
83.0 MPa

@Temperature 120 °C
12000 psi

@Temperature 248 °F
ISO Data
110 MPa

@Temperature 80.0 °C
16000 psi

@Temperature 176 °F
ISO Data
110 MPa

@Temperature 80.0 °C
16000 psi

@Temperature 176 °F
ASTM Test
283 MPa

@Temperature -40.0 °C
41000 psi

@Temperature -40.0 °F
ASTM Test
283 MPa

@Temperature -40.0 °C
41000 psi

@Temperature -40.0 °F
ISO Data
Tensile Strength, Ultimate 185 MPa
26800 psi
5mm/min; ISO 527
Elongation at Break 3.5 %
3.5 %
5mm/min; ISO 527
3.5 %
3.5 %
0.2 in/min; ASTM Test
3.6 %

@Temperature -40.0 °C
3.6 %

@Temperature -40.0 °F
ASTM Test
3.6 %

@Temperature -40.0 °C
3.6 %

@Temperature -40.0 °F
ISO Data
7.0 %

@Temperature 120 °C
7.0 %

@Temperature 248 °F
ISO Data
7.0 %

@Temperature 80.0 °C
7.0 %

@Temperature 176 °F
ISO Data
7.0 %

@Temperature 120 °C
7.0 %

@Temperature 248 °F
ASTM Test
7.0 %

@Temperature 80.0 °C
7.0 %

@Temperature 176 °F
ASTM Test
Tensile Modulus 10.1 GPa
1460 ksi
1mm/min; ISO 527
3.55 GPa

@Temperature 120 °C
515 ksi

@Temperature 248 °F
ISO Data
4.43 GPa

@Temperature 80.0 °C
643 ksi

@Temperature 176 °F
ISO Data
10.5 GPa

@Temperature -40.0 °C
1520 ksi

@Temperature -40.0 °F
ISO Data
Flexural Strength 260 MPa
37700 psi
ISO Data
297 MPa
43100 psi
ASTM Test
112 MPa

@Temperature 120 °C
16200 psi

@Temperature 248 °F
ASTM Test
140 MPa

@Temperature 93.0 °C
20300 psi

@Temperature 199 °F
ASTM Test
160 MPa

@Temperature 65.0 °C
23200 psi

@Temperature 149 °F
ASTM Test
380 MPa

@Temperature -40.0 °C
55100 psi

@Temperature -40.0 °F
ASTM Test
Flexural Modulus 8.20 GPa
1190 ksi
ISO Data
9.04 GPa
1310 ksi
ASTM Test
3.32 GPa

@Temperature 120 °C
482 ksi

@Temperature 248 °F
ASTM Test
3.75 GPa

@Temperature 93.0 °C
544 ksi

@Temperature 199 °F
ASTM Test
4.02 GPa

@Temperature 65.0 °C
583 ksi

@Temperature 149 °F
ASTM Test
Izod Impact, Notched 1.07 J/cm

@Temperature -40.0 °C
2.00 ft-lb/in

@Temperature -40.0 °F
ASTM Test
1.48 J/cm

@Thickness 3.17 mm
2.77 ft-lb/in

@Thickness 0.125 in
ASTM Test
Izod Impact, Unnotched 13.7 J/cm
25.7 ft-lb/in
ASTM Test
Izod Impact, Notched (ISO) 10.0 kJ/m²
4.76 ft-lb/in²
ISO Test
8.50 kJ/m²

@Temperature -40.0 °C
4.04 ft-lb/in²

@Temperature -40.0 °F
ISO Test
Charpy Impact Unnotched 8.80 J/cm²
41.9 ft-lb/in²
ISO 179
Charpy Impact, Notched 1.50 J/cm²
7.14 ft-lb/in²
ISO 179
1.00 J/cm²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 179
Thermal Properties Metric English Comments
CTE, linear 38.0 µm/m-°C

@Temperature -30.0 - 30.0 °C
21.1 µin/in-°F

@Temperature -22.0 - 86.0 °F
ASTM Test
CTE, linear, Parallel to Flow 21.0 µm/m-°C
11.7 µin/in-°F
ISO 11359
CTE, linear, Transverse to Flow 70.0 µm/m-°C
38.9 µin/in-°F
ISO 11359
Specific Heat Capacity 2.434 J/g-°C
0.5817 BTU/lb-°F
Melt
Thermal Conductivity 0.275 W/m-K
1.91 BTU-in/hr-ft²-°F
Melt
Melting Point 220 °C
428 °F
10 K/min
220 °C
428 °F
ASTM Test
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75
218 °C
424 °F
ASTM Test
Deflection Temperature at 1.8 MPa (264 psi) 205 °C
401 °F
ISO 75
210 °C
410 °F
ASTM Test
Flammability, UL94 HB

@Thickness 0.710 mm
HB

@Thickness 0.0280 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+13 ohm-cm
>= 1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
IEC 60250
3.7

@Frequency 1.00e+6 Hz
3.7

@Frequency 1.00e+6 Hz
ASTM Data
3.8

@Frequency 1e+9 Hz
3.8

@Frequency 1e+9 Hz
ASTM Data
4.2

@Frequency 100 Hz
4.2

@Frequency 100 Hz
IEC 60250
Dielectric Strength 44.0 kV/mm
1120 kV/in
IEC 60243-1
Dissipation Factor 0.010

@Frequency 1e+9 Hz
0.010

@Frequency 1e+9 Hz
ASTM Data
0.010

@Frequency 1.00e+6 Hz
0.010

@Frequency 1.00e+6 Hz
ASTM Data
0.020

@Frequency 1.00e+6 Hz
0.020

@Frequency 1.00e+6 Hz
IEC 60250
0.020

@Frequency 100 Hz
0.020

@Frequency 100 Hz
IEC 60250
Descriptive Properties Value Comments
Color Natural
Commercial Status Active America
Form Pellets
Impact Modified No
Primary Processing Technique Injection Molding
Processing Injection Molding
Special characteristic Heat stabilized or stable to heat
UL.UL-C Yes