Unitika BV2120 PA66, Flame Retardant, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika BV2120 PA66, Flame Retardant, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm @Thickness 3.20 mm |
0.015 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm @Thickness 3.20 mm |
0.017 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 115 | 115 | ISO 2039 |
| Tensile Strength at Break | 77.0 MPa | 11200 psi | ISO 527-1/-2 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527-1/-2 |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 3.20 GPa | 464 ksi | ISO 178 |
| Charpy Impact Unnotched | 4.10 J/cm² | 19.5 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 108 °C | 226 °F | ISO 75-1/-2 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.6 @Frequency 1.00e+6 Hz |
3.6 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 25.0 kV/mm @Thickness 1.00 mm |
635 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.010 @Frequency 1.00e+6 Hz |
0.010 @Frequency 1.00e+6 Hz |
IEC 60250 |
Users viewing this material also viewed the following:
- PolyOne Maxxam™ DP 9052-3-1000 Polyethylene, High Density (HDPE)
- Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes
- SABIC Innovative Plastics ULTEM DU319 PEI
- Goodfellow Cobalt/Silicon/Boron/Iron/Nickel Alloy
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR N330 (HAF) Black
- AK Steel 301 Austenitic Stainless steel
- 3M 5850 Clean-View Pad
- Polyram PlusTek RA320G6 Nylon 6.6, 30% Glass Fiber, Flame Retardant
- A. Schulman POLYBLAK™ 3123 Premium Black Color Concentrate, 50% Carbon Black Based In LDPE
Copyright © lookpolymers.com All Rights Reserved