- Unitika A1030GFL45 PA6, 45% Glass Fiber Reinforced, Dry
Unitika A1030GFL45 PA6, 45% Glass Fiber Reinforced, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled |
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Unitika A1030GFL45 PA6, 45% Glass Fiber Reinforced, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183 |
| Water Absorption | 1.0 % @Time 86400 sec |
1.0 % @Time 24.0 hour |
ISO 62 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Thickness 3.20 mm |
0.0010 in/in @Thickness 0.126 in |
|
| Linear Mold Shrinkage, Transverse | 0.0030 cm/cm @Thickness 3.20 mm |
0.0030 in/in @Thickness 0.126 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 122 | 122 | ISO 2039 |
| Tensile Strength at Break | 210 MPa | 30500 psi | ISO 527-1/-2 |
| Elongation at Break | 2.9 % | 2.9 % | ISO 527-1/-2 |
| Tensile Modulus | 13.6 GPa | 1970 ksi | ISO 527-1/-2 |
| Flexural Strength | 325 MPa | 47100 psi | ISO 178 |
| Flexural Modulus | 12.4 GPa | 1800 ksi | ISO 178 |
| Charpy Impact Unnotched | 7.90 J/cm² | 37.6 ft-lb/in² | ISO 179-1 |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179-1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 23.0 µm/m-°C | 12.8 µin/in-°F | ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB @Thickness 0.860 mm |
HB @Thickness 0.0339 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+13 ohm-cm | 2.00e+13 ohm-cm | IEC 60093 |
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz |
3.3 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Dielectric Strength | 42.1 kV/mm @Thickness 1.00 mm |
1070 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.022 @Frequency 1.00e+6 Hz |
0.022 @Frequency 1.00e+6 Hz |
IEC 60250 |
| Comparative Tracking Index | 550 V | 550 V | IEC 60112 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CX5430 PC+ABS (Asia Pacific)
- IDI Composites C-105 Thermoset Polyester, Molding
- Ineos Innovene H07B-00 Polypropylene Homopolymer
- Saint-Gobain Chemlam® RL® RL5000 PTFE-Coated Non-woven Aramid Reinforced Laminate
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 20 PHR Non-Black, Aerosil 200
- Hexcel® Redux® 335M Adhesive film for bonding metallic and composite components (0.06 psf)
- ExxonMobil LDPE LD 158BW Low Density Polyethylene Resin
- Ashley Polymers Ashlene® 520-50G Nylon 66, 50% Glass Reinforced
- Polyplastic Armamid® PA6 GF 30 HS-901 Nylon, 30% Glass Filled
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 4.0 PHR MBT
Copyright © lookpolymers.com All Rights Reserved