- Lehmann & Voss LUVOCOM® 1700-8126 PPO, with glass spheres and PTFE
Lehmann & Voss LUVOCOM® 1700-8126 PPO, with glass spheres and PTFE
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, PTFE Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1700-8126 PPO, with glass spheres and PTFE.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High dimensionally stable precision parts, even at elevated temperatures and narrow tolerance range.Isotropic shrinkage characteristics.Improved friction and wear behaviour. Emergency running property.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.43 g/cc | 1.43 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 58.0 MPa | 8410 psi | |
| Elongation at Yield | 3.2 % | 3.2 % | |
| 4.2 % | 4.2 % | flexural | |
| Modulus of Elasticity | 3.50 GPa | 508 ksi | |
| Flexural Strength | 85.0 MPa | 12300 psi | |
| Flexural Modulus | 2.90 GPa | 421 ksi | |
| Charpy Impact Unnotched | 2.20 J/cm² | 10.5 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 110 °C | 230 °F | |
| 130 °C | 266 °F | short term | |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm | |
| Insulation Resistance | >= 1.00e+12 ohm | >= 1.00e+12 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 280 °C | 536 °F | mass temp |
| Nozzle Temperature | 285 - 295 °C | 545 - 563 °F | |
| Zone 1 | 270 - 280 °C | 518 - 536 °F | |
| Zone 2 | 270 - 300 °C | 518 - 572 °F | |
| Zone 3 | 290 - 305 °C | 554 - 581 °F | |
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | |
| Drying Temperature | 95.0 - 110 °C @Time <=7200 sec |
203 - 230 °F @Time <=2.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible A5DUB Polyvinyl Chloride, Flexible (PVC, Flexible)
- Teknor Apex Monprene® MP-2745 Thermoplastic Elastomer
- TIMET TIMETAL® 551 (Ti-4Al-4Mo-4Sn-0.5Si) Titanium Alloy; 25-100 mm
- Domo 1101P Polypropylene Homopolymer
- DuPont Teijin Films Melinex® D316 Polyester Film, 200 Gauge
- Eurotec® Tecomid® NB40 NL RM PA6, unfilled, MoS2, natural
- Aaron Industries AAROLENE® ARPP C 200-2 Polypropylene Compounded Resin
- 3M 519YP Sandblast Stencil
- Solvay Specialty Polymers Solef® 1009 PVDF Homopolymer (discontinued **)
- Petroquimica Triunfo Trithene® JX 7300 LDPE - Injection Molding
Copyright © lookpolymers.com All Rights Reserved