ExxonMobil Santoprene® 121-75M100 Thermoplastic Elastomer

Category Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Vulcanizate Elastomer (TPV)
Manufacturer Exxon Chemical
Trade Name Santoprene®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil Santoprene® 121-75M100 Thermoplastic Elastomer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A soft, black, UV resistant thermoplastic vulcanizate (TPV) in the thermoplastic elastomer (TPE) family. This material combines good physical properties and chemical resistance for use in difficult injection molding applications. This grade of Santoprene TPV is shear-dependent and can be processed on conventional thermoplastics equipment for injection molding. It is polyolefin based and completely recyclable.Key Features:Used in glass encapsulation applications.Designed for fast, easy injection molding, especially for complex part geometries.Used in sealing applications.Recommended for applications requiring superior part surface appearance.UL listed: file #QMFZ2.E80017, Plastics - Component; file #QMFZ8.E80017, Plastics Certified For Canada - Component.Although not NSF certified, this product has a Material Supplier Form on file with NSF to facilitate its evaluation for use in applications requiring NSF certification.EU and China RoHS compliant.Applications:Automotive- Interior Mat, Seals, Gaskets and Weather SealsUses:Automotive Applications Automotive Interior Trim Automotive Exterior Trim Automotive Under the HoodAvailability: Africa & Middle East, Europe, North America, Asia Pacific, Latin America and South AmericaInformation provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Specific Gravity 0.920 g/cc
0.920 g/cc
23°C; ASTM D792
Mechanical Properties Metric English Comments
Hardness, Shore A 80
80
2 mm, 15 sec; ISO 868
82
82
Air at 302°F, 168 hr; ASTM D573
Tensile Strength at Break 6.259 MPa
907.8 psi
Air at 302°F, 168 hr; ASTM D573
7.03 MPa
1020 psi
Across Flow; ASTM D412
Elongation at Break 412.8 %
412.8 %
Air at 302°F, 168 hr; ASTM D573
480 %
480 %
Across Flow; ASTM D412
Tear Strength 25.9 kN/m
148 pli
73°F, Die C, Across Flow; ASTM D624
Compression Set 40 %
40 %
158°F, 22 hr; ASTM D395
53 %
53 %
257°F, 70 hr; ASTM D395
Thermal Properties Metric English Comments
Brittleness Temperature -60.0 °C
-76.0 °F
ASTM D746
Processing Properties Metric English Comments
Processing Temperature 175 - 230 °C
347 - 446 °F
Rear Barrel Temperature 182 °C
360 °F
Middle Barrel Temperature 188 °C
370 °F
Front Barrel Temperature 193 °C
380 °F
Nozzle Temperature 199 °C
390 °F
Melt Temperature 204 - 232 °C
400 - 450 °F
Processing
Mold Temperature 10.0 - 51.7 °C
50.0 - 125 °F
Processing
Drying Temperature 82.2 °C
180 °F
Dry Time 3 hour
3 hour
Moisture Content 0.080 %
0.080 %
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Processing
Clamp Pressure 41.4 - 68.9 MPa
6000 - 10000 psi
Vent Depth 0.00254 cm
0.00100 in
Cushion 0.317 - 0.635 cm
0.125 - 0.250 in
Screw Speed 100 - 200 rpm
100 - 200 rpm
Descriptive Properties Value Comments
Color Black
Form Pellets
Injection Rate Fast
Maximum Regrind % 20
Screw Compression Ratio 2:1 - 2.5:1
Screw L/D Ratio 16:1 - 20:1