SABIC Innovative Plastics LNP COLORCOMP J1000E PES (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name LNP Colorcomp
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics LNP COLORCOMP J1000E PES (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
LNP* COLORCOMP* J1000E is a compound based on PES resin. Added features include: Easy Moulding.
Physical Properties Metric English Comments
Density 1.37 g/cc
0.0495 lb/in³
ISO 1183
Water Absorption 0.90 %

@Time 86400 sec
 0.90 %

@Time 24.0 hour
 ISO 62-1
Linear Mold Shrinkage, Flow 0.0090 cm/cm
0.0090 in/in
SABIC Method
Mechanical Properties Metric English Comments
Tensile Strength at Break 65.0 MPa
9430 psi
50 mm/min; ISO 527
Tensile Strength, Yield 91.0 MPa
13200 psi
50 mm/min; ISO 527
Elongation at Yield 6.8 %
6.8 %
50 mm/min; ISO 527
Tensile Modulus 2.70 GPa
392 ksi
1 mm/min; ISO 527
Flexural Yield Strength 136 MPa
19700 psi
2 mm/min; ISO 178
Flexural Modulus 2.80 GPa
406 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 7.00 kJ/m²
3.33 ft-lb/in²
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) NB
NB
80*10*4; ISO 180/1U
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 56.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 31.1 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 57.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 31.7 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 197 °C
387 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af