Toyobo PELPRENE™ P95C Polyester TPE, High Flexibility, High Melting Point
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P95C Polyester TPE, High Flexibility, High Melting Point.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, High Flexibility, High Melting PointInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.45 % | 0.45 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.0080 cm/cm @Thickness 2.00 mm |
0.0080 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 17 g/10 min @Temperature 230 °C |
17 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 95 | 95 | JIS K6301 |
| Hardness, Shore D | 41 | 41 | ASTM D2240 |
| Tensile Strength at Break | 27.0 MPa | 3920 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| 50% Modulus | 0.00830 GPa | 1.20 ksi | ASTM D638 |
| Flexural Modulus | 0.0740 GPa | 10.7 ksi | ASTM D790 |
| Compressive Modulus | 0.00760 GPa | 1.10 ksi | 0.1; ASTM D695 |
| Resilience | 75 | 75 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 108 kN/m | 616 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 17 | 17 | ASTM D1044 |
| Compression Set | 52 % | 52 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 170 µm/m-°C @Temperature 20.0 °C |
94.4 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 213 °C | 415 °F | By DSC |
| Maximum Service Temperature, Air | <= 25.0 °C | <= 77.0 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 162 °C | 324 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 9.00e+12 ohm-cm | 9.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- ExxonMobil Santoprene® 8123-45S100 Thermoplastic Elastomer (discontinued **)
- Lehmann & Voss LUVOCOM® 80-8268 Polyacetal-copolymer, with PTFE, lubricant modified
- Hybrid Plastics FireQuench® PM 1287 Resin
- Gouda Vuurvast AK 82 A Dense Refractory Brick
- Indorama StarPet Preformance® ES11 PET Resin
- Washington Penn PPH2CF2 Polypropylene, 20% Calcium Carbonate Reinforced
- EMS-Grivory Grivory® BG-30 S FA PA6-GF30
- ExxonMobil Exxtral™ BNT 010 Performance Polyolefin
- BASF Ultramid® A3HG7 35% Glass Filled PA66 (Conditioned)
- Asahi Glass Fluon® AH-3000 LM-ETFE, Conductive Type, Fluororesin
Copyright © lookpolymers.com All Rights Reserved