Toyobo PELPRENE™ P48U Polyester TPE, Weather-resistant
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyester TPE , Polyester, TP , Polyester Thermoplastic Elastomer |
| Manufacturer | Toyobo |
| Trade Name | Pelprene™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo PELPRENE™ P48U Polyester TPE, Weather-resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features: Polyester TPE, Weather-resistantInformation provided by Toyobo.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.47 % | 0.47 % | 23°C, 65% RH |
| Linear Mold Shrinkage | 0.0060 cm/cm @Thickness 2.00 mm |
0.0060 in/in @Thickness 0.0787 in |
|
| Melt Index of Compound | 25 g/10 min @Temperature 230 °C |
25 g/10 min @Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 92 | 92 | JIS K6301 |
| Hardness, Shore D | 41 | 41 | ASTM D2240 |
| Tensile Strength at Break | 26.0 MPa | 3770 psi | ASTM D638 |
| Elongation at Break | 700 % | 700 % | ASTM D638 |
| 50% Modulus | 0.00830 GPa | 1.20 ksi | ASTM D638 |
| Flexural Modulus | 0.0630 GPa | 9.14 ksi | ASTM D790 |
| Compressive Modulus | 0.00610 GPa | 0.885 ksi | 0.1; ASTM D695 |
| Resilience | 76 | 76 | JIS K6301 |
| Izod Impact, Notched | NB | NB | ASTM D256 |
| Tear Strength | 103 kN/m | 588 pli | ASTM D624 |
| Taber Abrasion, mg/1000 Cycles | 17 | 17 | ASTM D1044 |
| Compression Set | 51 % | 51 % | JIS K6301 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 170 µm/m-°C @Temperature 20.0 °C |
94.4 µin/in-°F @Temperature 68.0 °F |
TMA |
| Melting Point | 176 °C | 349 °F | By DSC |
| Maximum Service Temperature, Air | <= 25.0 °C | <= 77.0 °F | Heat deflection temperature, load unknown; ASTM D648 |
| Vicat Softening Point | 130 °C | 266 °F | ASTM D1525 |
| Brittleness Temperature | <= -65.0 °C | <= -85.0 °F | JIS K6301 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+12 ohm-cm | 4.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | JIS K2111 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1200-22 Fiberglass Reinforced Thermoset SMC
- SABIC Innovative Plastics Cycoloy® C6600 PC+ABS
- Solvay TECHNYL® C 246SI V11 PA6, 11% glass filled, DRY
- Taiwan Sheen Soon Sheenthane® AS-632H TPU for PU Adhesive
- Solvay Chemicals SOLKAFLAM® 125 UL
- Borealis CA8200 Low Density Polyethylene
- Polyram RamShine PW311G4 SAN, 20% Glass Fiber
- Bohler-Uddeholm BÖHLER M303 EXTRA Plastic Mold Steel
- BASF Ultramid® KR 4355 G5 BK 00564 25% Glass Filled PA6/6T (Conditioned)
- Beijing Evergrow Resources UHF-BF1500 UHMW PE Fiber
Copyright © lookpolymers.com All Rights Reserved