Toyobo GLAMIDE® TY-835TC Nylon-66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Mineral Filled |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® TY-835TC Nylon-66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade TY-835TC is a mineral-reinforced Nylon-66 with a fine surface and thermal discoloration resistance.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 20 % | 20 % | |
| Water Absorption | 0.50 % | 0.50 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm @Thickness 1.00 mm |
0.0030 - 0.0060 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.0060 - 0.010 cm/cm @Thickness 3.00 mm |
0.0060 - 0.010 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 25 g/10 min | 25 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 40.0 MPa @Temperature 80.0 °C |
5800 psi @Temperature 176 °F |
Practical Use; ASTM-D638 |
| 48.0 MPa @Temperature 80.0 °C |
6960 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 58.0 MPa @Temperature 23.0 °C |
8410 psi @Temperature 73.4 °F |
Practical Use; ASTM-D638 | |
| 80.0 MPa @Temperature 23.0 °C |
11600 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 96.0 MPa @Temperature -40.0 °C |
13900 psi @Temperature -40.0 °F |
Practical Use; ASTM-D638 | |
| 100 MPa @Temperature -40.0 °C |
14500 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 5.2 % | 5.2 % | Absolute Drying; ASTM-D638 |
| 8.0 % | 8.0 % | Practical Use; ASTM-D638 | |
| Flexural Strength | 57.0 MPa @Temperature 80.0 °C |
8270 psi @Temperature 176 °F |
Practical Use; ASTM-D790 |
| 80.0 MPa @Temperature 80.0 °C |
11600 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 90.0 MPa @Temperature 23.0 °C |
13100 psi @Temperature 73.4 °F |
Practical Use; ASTM-D790 | |
| 130 MPa @Temperature 23.0 °C |
18900 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 153 MPa @Temperature -40.0 °C |
22200 psi @Temperature -40.0 °F |
Practical Use; ASTM-D790 | |
| 160 MPa @Temperature -40.0 °C |
23200 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 1.60 GPa @Temperature 80.0 °C |
232 ksi @Temperature 176 °F |
Practical Use; ASTM-D790 |
| 3.50 GPa @Temperature 80.0 °C |
508 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 3.80 GPa @Temperature 23.0 °C |
551 ksi @Temperature 73.4 °F |
Practical Use; ASTM-D790 | |
| 5.30 GPa @Temperature 23.0 °C |
769 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 5.60 GPa @Temperature -40.0 °C |
812 ksi @Temperature -40.0 °F |
Practical Use; ASTM-D790 | |
| 6.40 GPa @Temperature -40.0 °C |
928 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Compressive Strength | 62.0 MPa | 8990 psi | Practical Use; ASTM-D695 |
| 90.0 MPa | 13100 psi | Absolute Drying; ASTM-D695 | |
| Izod Impact, Notched | 0.200 J/cm @Temperature 23.0 °C |
0.375 ft-lb/in @Temperature 73.4 °F |
Practical Use; ASTM-D256 |
| 0.350 J/cm @Temperature -40.0 °C |
0.656 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 | |
| 0.450 J/cm @Temperature -40.0 °C |
0.843 ft-lb/in @Temperature -40.0 °F |
Practical Use; ASTM-D256 | |
| 0.530 J/cm @Temperature 23.0 °C |
0.993 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17, Absolute Drying; ASTM-D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 58.0 µm/m-°C | 32.2 µin/in-°F | Absolute Drying; ASTM-D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 245 °C | 473 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | Practical Use; ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 16.0 kV/mm @Thickness 2.00 mm |
406 kV/in @Thickness 0.0787 in |
2mmt, Practical Use; ASTM-D149 |
| 24.0 kV/mm @Thickness 2.00 mm |
610 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 120 sec | 120 sec | Practical Use; ASTM-D495 |
| 130 sec | 130 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 300 °C | 518 - 572 °F | |
| Mold Temperature | 60.0 °C | 140 °F | |
| Injection Pressure | 30.0 - 60.0 MPa | 4350 - 8700 psi |
Users viewing this material also viewed the following:
- MV Labs TE250 (NH4)2TeBr6 Ammonium hexabromotellurate(IV)
- PolyOne OnForce™ LFT NN-40LCF/001 Grey Polyamide 66 (Nylon 66)
- Solvay Specialty Polymers Amodel® A-1133 NL WH 505 Polyphthalamide (PPA) (Unverified Data**)
- A. Schulman POLYBATCH™ Red 5400 Concentrate Based In Polyethylene
- Fainplast Compounds PM 5526/1 Flexible PVC, Lead Free
- Bapolene® 0760 Polyethylene, Blow Molding Grade
- Carpenter AerMet®-for-Tooling Tool Steel, Double Aged 468°C
- Axiall 13872 Wire & Cable Flexible PVC
- Axiall 4420 Flexible PVC
- Azoty Tarnow™ Alphalon™ 24 Nylon 6
Copyright © lookpolymers.com All Rights Reserved