- FKuR Kunststoff Fibrolon® P 7550 Wood-Plastic Compound, Fiber Reinforced
FKuR Kunststoff Fibrolon® P 7550 Wood-Plastic Compound, Fiber Reinforced
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Polypropylene (PP) , Wood and Natural Products |
| Manufacturer | FKuR Kunststoff GmbH |
| Trade Name | Fibrolon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | FKuR Kunststoff Fibrolon® P 7550 Wood-Plastic Compound, Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FIBROLON® are fiber reinforced compounds. Fibrolon® P 7550 has a polypropylene base. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-Composites: WPC), which, unlike many other WPC, can be injection molded without problems. Furthermore it is possible to process FIBROLON® to complex profiles, panels and hollow profiles and/or into components for the automotive interiors. FIBROLON® compounds are distinguished by high strength and a stiffness comparable to wood.Information Provided by FKuR Kunststoff GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.460 g/cc | 0.0166 lb/in³ | ISO 60 |
| Density | 1.03 g/cc | 0.0372 lb/in³ | ISO 1183 |
| Melt Flow | 13 - 15 g/10 min @Load 5.00 kg, Temperature 230 °C |
13 - 15 g/10 min @Load 11.0 lb, Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 22.0 MPa | 3190 psi | ISO 527 |
| Tensile Strength, Yield | 22.0 MPa | 3190 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 3.25 GPa | 471 ksi | ISO 527 |
| Flexural Yield Strength | 32.0 MPa | 4640 psi | at 3.5% strain; 4% strain at break; ISO 178 |
| Flexural Modulus | 3.55 GPa | 515 ksi | ISO 178 |
| Charpy Impact Unnotched | 0.790 J/cm² @Temperature 23.0 °C |
3.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eU |
| Charpy Impact, Notched | 0.330 J/cm² @Temperature 23.0 °C |
1.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 150 - 180 °C | 302 - 356 °F | ISO 3146-C |
| Vicat Softening Point | 139 °C | 282 °F | A; ISO 306 |
Users viewing this material also viewed the following:
- Nabaltec NABALOX® NO 105-71 RA Calcined Aluminum Oxide
- SABIC Innovative Plastics LNP LUBRICOMP RL002 PA 66 (Europe-Africa-Middle East)
- Silberline Lansford 243 Standard Series
- A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene
- ThyssenKrupp 75Cr1 Saw Steel, Four-High Mill Plate
- Wellman Wellamid® FRGF1827-BK1 10% Glass Fiber Reinforced Flame Retardant Nylon 66
- Eagle Brass 521 Phosphor Bronzes 8% C, Extra Spring
- Colorite Polymers Self Frosting™ 9511SF Vinyl Compound
- Axiall 9175 White 10 Rigid PVC, Molding, White 10
Copyright © lookpolymers.com All Rights Reserved