Toyobo GLAMIDE® NB-5550 Nylon/Olefin
| Category | Polymer , Thermoplastic , Nylon |
| Manufacturer | Toyobo |
| Trade Name | GLAMIDE® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Toyobo GLAMIDE® NB-5550 Nylon/Olefin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
GLAMIDE® is very tough and exhibits high abrasion resistance. It has a high melting point and heat resistance, has well-balanced proportions of mechanical properties, performs self-distinguishing and a specific grade approved as UL94V-0 class is provided, and it exhibits excellent chemical resistance and oil resistance. Grade NB-5550 is a light weight, mineral-reinforced alloy of nylon and olefin with a good appearance and low water absorption.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | Absolute Drying; ASTM-D792 |
| Filler Content | 30 % | 30 % | |
| Water Absorption | 0.40 % | 0.40 % | Absolute Drying; ASTM-D570 |
| Moisture Absorption at Equilibrium | 1.7 % | 1.7 % | Absolute Drying; ASTM-D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm @Thickness 1.00 mm |
0.0040 - 0.0070 in/in @Thickness 0.0394 in |
Absolute Drying |
| 0.012 - 0.016 cm/cm @Thickness 3.00 mm |
0.012 - 0.016 in/in @Thickness 0.118 in |
Absolute Drying | |
| Melt Flow | 5.0 g/10 min | 5.0 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | Absolute Drying; ASTM-D785 |
| Tensile Strength, Ultimate | 28.0 MPa @Temperature 80.0 °C |
4060 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.7%); ASTM-D638 |
| 31.0 MPa @Temperature 80.0 °C |
4500 psi @Temperature 176 °F |
Absolute Drying; ASTM-D638 | |
| 55.0 MPa @Temperature 23.0 °C |
7980 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.7%); ASTM-D638 | |
| 66.0 MPa @Temperature 23.0 °C |
9570 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D638 | |
| 100 MPa @Temperature -40.0 °C |
14500 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.7%); ASTM-D638 | |
| 110 MPa @Temperature -40.0 °C |
16000 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D638 | |
| Elongation at Break | 3.8 % | 3.8 % | Absolute Drying; ASTM-D638 |
| Flexural Strength | 35.0 MPa @Temperature 80.0 °C |
5080 psi @Temperature 176 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 |
| 50.0 MPa @Temperature 80.0 °C |
7250 psi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 85.0 MPa @Temperature 23.0 °C |
12300 psi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 | |
| 105 MPa @Temperature 23.0 °C |
15200 psi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 163 MPa @Temperature -40.0 °C |
23600 psi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 | |
| 170 MPa @Temperature -40.0 °C |
24700 psi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Flexural Modulus | 1.50 GPa @Temperature 80.0 °C |
218 ksi @Temperature 176 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 |
| 3.20 GPa @Temperature 80.0 °C |
464 ksi @Temperature 176 °F |
Absolute Drying; ASTM-D790 | |
| 3.80 GPa @Temperature 23.0 °C |
551 ksi @Temperature 73.4 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 | |
| 5.10 GPa @Temperature 23.0 °C |
740 ksi @Temperature 73.4 °F |
Absolute Drying; ASTM-D790 | |
| 7.20 GPa @Temperature -40.0 °C |
1040 ksi @Temperature -40.0 °F |
Practical Use (Water Absorption 1.7%); ASTM-D790 | |
| 8.00 GPa @Temperature -40.0 °C |
1160 ksi @Temperature -40.0 °F |
Absolute Drying; ASTM-D790 | |
| Izod Impact, Notched | 0.380 J/cm @Temperature -40.0 °C |
0.712 ft-lb/in @Temperature -40.0 °F |
Absolute Drying; ASTM-D256 |
| 0.500 J/cm @Temperature 23.0 °C |
0.937 ft-lb/in @Temperature 73.4 °F |
Absolute Drying; ASTM-D256 | |
| 0.650 J/cm @Temperature -40.0 °C |
1.22 ft-lb/in @Temperature -40.0 °F |
Practical Use (Water Absorption 1.7%); ASTM-D256 | |
| 2.00 J/cm @Temperature 23.0 °C |
3.75 ft-lb/in @Temperature 73.4 °F |
Practical Use (Water Absorption 1.7%); ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 202 °C | 396 °F | Absolute Drying; ASTM-D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 119 °C | 246 °F | Absolute Drying; ASTM-D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+9 ohm-cm | 1.00e+9 ohm-cm | Practical Use (Water Absorption 1.7%); ASTM-D257 |
| 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | Absolute Drying; ASTM-D257 | |
| Dielectric Strength | 23.0 kV/mm @Thickness 2.00 mm |
584 kV/in @Thickness 0.0787 in |
Practical Use (Water Absorption 1.7%); ASTM-D149 |
| 30.0 kV/mm @Thickness 2.00 mm |
762 kV/in @Thickness 0.0787 in |
Absolute Drying; ASTM-D149 | |
| Arc Resistance | 120 sec | 120 sec | Practical Use (Water Absorption 1.7%); ASTM-D495 |
| 130 sec | 130 sec | Absolute Drying; ASTM-D495 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC Method |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 240 - 290 °C | 464 - 554 °F | |
| Mold Temperature | 50.0 - 120 °C | 122 - 248 °F | |
| Injection Pressure | 50.0 MPa | 7250 psi |
Users viewing this material also viewed the following:
- Nye Lubricants 500F (RS) Synthetic Oil
- Inno-Comp INNOPOL® CS 2-9514 10% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer
- Greene Tweed Arlon® 2000 Polyketone
- Haynes 214® alloy, 50% cold reduction
- LyondellBasell Adflexâ„¢ Q 200 F Polyolefin
- Lucas-Milhaupt Silvaloy® 18M Brazing Alloy
- Samsung Cheil Industries Infino® UF-1013 PC, Unreinforced FR
- A. Schulman POLYBATCH™ White 8750 Concentrate Based In HDPE
- Hexcel® HexForce™ 1581 Fiber Glass Fabric
- Ravago Manufacturing Americas Echo® RPPC 20/2 BK Recycled Polypropylene
Copyright © lookpolymers.com All Rights Reserved