SABIC Innovative Plastics LNP Stat-kon DEL369E PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP STAT-KON |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Stat-kon DEL369E PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Stat-Kon* DEL369E is a compound based on Polycarbonate containing Carbon Fiber and PTFE. Characteristics of this grade are Flame Retardant and Statically Conductive.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| 1.479 g/cc | 0.05343 lb/in³ | ASTM D 792 | |
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | 23°C / 50% RH; ISO 62 |
| 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
50% RH; ASTM D 570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 132 MPa | 19100 psi | 5 mm/min; ISO 527 |
| 133 MPa | 19300 psi | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Strength, Yield | 132 MPa | 19100 psi | 5 mm/min; ISO 527 |
| 133 MPa | 19300 psi | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Break | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D 638 | |
| Elongation at Yield | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| 1.2 % | 1.2 % | Type I, 5 mm/min; ASTM D 638 | |
| Tensile Modulus | 21.84 GPa | 3168 ksi | 1 mm/min; ISO 527 |
| 22.6 GPa | 3280 ksi | 50 mm/min; ASTM D 638 | |
| Flexural Strength | 195 MPa | 28300 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 15.76 GPa | 2286 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| 17.21 GPa | 2496 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.580 J/cm @Temperature 23.0 °C |
1.09 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 4.08 J/cm @Temperature 23.0 °C |
7.64 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 24.0 kJ/m² @Temperature 23.0 °C |
11.4 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 149 °C @Thickness 3.20 mm |
300 °F @Thickness 0.126 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 143 °C @Thickness 3.20 mm |
289 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 - 10000 ohm | 10 - 10000 ohm | ASTM D 257 |
Users viewing this material also viewed the following:
- Nitriflex SB-1013G Styrene Butadiene Copolymer
- LyondellBasell Hifaxâ„¢ CB251 Thermoplastic Polyolefin Elastomer
- Solvay Specialty Polymers Kalix® 5950 HFFR Polyamide, High Performance (HPPA), 50% Glass Fiber
- Saint-Gobain Norton® T-200 Mechanical Grade PTFE Sheet (0.250" thick)
- Teknor Apex APEX® 90-A41R-60-NT Polyvinyl Chloride, Flexible
- Zircar Zirconia M-45 Alumina Boards, Discs & Cylinders Insulation
- Excalibar NewWate™ Barite BaSO4 Powder
- Aleris Hokotol Aluminum Alloy, 200 mm Thickness
- Arlon 48271R010 0.010" (0.254 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved