Total Lumicene® mPE BM359 SG Metallocene Medium Density High Gloss Blow Molding Resin

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , MDPE , Medium Density Polyethylene (MDPE), Film Grade
Manufacturer	Total Atofina
Trade Name	Lumicene® mPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total Lumicene® mPE BM359 SG Metallocene Medium Density High Gloss Blow Molding Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Metallocene Medium Density High Gloss Blow Molding ResinCharacteristics:Outstanding glossGood flexibilityExcellent impact strengthGood ESCRUSP Class VI compliantFDA CompliantApplications:Coextruded Glossy BottlesMonolayer Squeezable BottlesInjection Blow Molded ContainersInformation provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Density	0.935 g/cc	0.0338 lb/in³	ASTM D792
ESCR 100% Igepal®	>= 1000 hour	>= 1000 hour	F50; ASTM D1693, B
ESCR 10% Igepal®	>= 1000 hour	>= 1000 hour	F50; ASTM D1693, B
Melt Flow	0.90 g/10 min @Load 2.16 kg, Temperature 190 °C	0.90 g/10 min @Load 4.76 lb, Temperature 374 °F	ASTM D1238
	25 g/10 min @Load 21.6 kg, Temperature 190 °C	25 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	27.6 MPa	4000 psi	ASTM D638
Elongation at Break	>= 600 %	>= 600 %	ASTM D638
Flexural Modulus	0.738 GPa	107 ksi	ASTM D790
Izod Impact, Notched	5.61 J/cm	10.5 ft-lb/in	ASTM D256
Impact Test	31.2 J @Temperature -20.0 °C	23.0 ft-lb @Temperature -4.00 °F	Cold Temperature Impact Energy; ASTM D3763

Thermal Properties	Metric	English	Comments
Melting Point	124 °C	255 °F	ASTM D3417

Optical Properties	Metric	English	Comments
Gloss	40 - 80 %	40 - 80 %	at 60°; TOTAL Method

Processing Properties	Metric	English	Comments
Melt Temperature	182 - 199 °C	360 - 390 °F	Extrusion

Descriptive Properties	Value	Comments
Process	Blow Molding
Region	US & Canada	Bamberger Polymers Distribution

Users viewing this material also viewed the following: