Total HDPE XT10B High Density Polyethylene, Pipe Resin

Category	Polymer , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Pipe Grade
Manufacturer	Total Atofina
Trade Name	HDPE
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total HDPE XT10B High Density Polyethylene, Pipe Resin.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Polyethylene: HDPE Bimodal PE4710 pipe resin (Black)Characteristics:Outstanding high temperature creep rupture strengthOutstanding slow crack growth resistanceExcellent resistance to rapid crack propagationNSF certified to D2513 (gas), CSA B137.4 (gas), CSA B137.1 (water) and CSA C448 (geothermal)NSF Standard 14/61 CertifiedApplications:Gas distributionPotable waterMolded fittingsIndustrial & miningGas and oil gatheringGeneral pipe reliningInformation provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.958 g/cc	0.958 g/cc	ASTM D792
Carbon Black Loading	2.5 %	2.5 %	ASTM D1603
Melt Flow	0.20 g/10 min @Load 5.00 kg, Temperature 190 °C	0.20 g/10 min @Load 11.0 lb, Temperature 374 °F	ASTM D1238
	7.0 g/10 min @Load 21.6 kg, Temperature 190 °C	7.0 g/10 min @Load 47.6 lb, Temperature 374 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
PENT	>= 1000 hour	>= 1000 hour	ASTM F1473
Tensile Strength, Yield	24.8 MPa	3600 psi	ASTM D638
Elongation at Break	>= 500 %	>= 500 %	ASTM D638
Flexural Modulus	1.10 GPa @Strain 1.00 %	160 ksi @Strain 1.00 %	ASTM D790
Hydrostatic Design Basis	6.89 MPa @Temperature 60.0 °C	1000 psi @Temperature 140 °F	ASTM D2837
	11.0 MPa @Temperature 22.8 °C	1600 psi @Temperature 73.0 °F	ASTM D2837

Thermal Properties	Metric	English	Comments
Melting Point	130 - 132 °C	266 - 270 °F	ASTM D3417

Descriptive Properties	Value	Comments
Cell Classification	445574C, 445576C	ASTM D3350
Minimum Required Strength	10 MPa	ISO 9080/ISO 12162
Pipe Test Category	CEC	ASTM D2513