Tipco Tipcofil® AG 300 - 15% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Tipco Industries Ltd., India |
| Trade Name | Tipcofil® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Tipco Tipcofil® AG 300 - 15% Glass Fiber Reinforced Nylon-6 Compound, with High Heat Stability.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
15% Glass Reinforced Nylon-6 CompoundApplications: General PurposeProcessing: Injection MoldingInformation provided by the Manufacturer, Tipco Industries Ltd.,
India.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Melt Flow | 16 g/10 min | 16 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 120 MPa | 17400 psi | ASTM D638 |
| Elongation at Break | >= 4.0 % | >= 4.0 % | ASTM D638 |
| Flexural Yield Strength | 175 MPa | 25400 psi | ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² | 3.09 ft-lb/in² | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 48.0 kJ/m² | 22.8 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ASTM D648 |
| Vicat Softening Point | 205 °C | 401 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 250 °C | 482 °F | |
| Rear Barrel Temperature | 245 °C | 473 °F | |
| Middle Barrel Temperature | 250 °C | 482 °F | |
| Front Barrel Temperature | 255 °C | 491 °F | |
| Nozzle Temperature | 250 °C | 482 °F | |
| Mold Temperature | 90.0 °C | 194 °F | |
| Drying Temperature | 85.0 °C | 185 °F |
Users viewing this material also viewed the following:
- PSM Industries Ferro-TiC® MS-5A Age Hardenable Martensitic Stainless Steel
- Mitsubishi Hostaphan® RN, 350 micron Nominal Thickness Universal Polyethylene Terephthalate Film
- H.C. Starck Amperit® 518.074 Agglomerated, Sintered Tungsten Carbide-Cobalt 88-12 (WC-CO)
- Saint-Gobain CHR® SG05-03(R) Premium Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- SABIC Innovative Plastics LNP VERTON WV006 PBT (Europe-Africa-Middle East)
- A. Schulman POLYTROPE™ TPP 503 Injection Molding Grade Olefinic Thermoplastic Elastomer
- Azoty Tarnow™ TARNOFORM 300 GF2 POM
- Adell ZR-37 33% Glass Reinforced Nylon/Olefin Alloy
- 3M Scotch-Weld™ 2290 Epoxy Adhesive/Coating
- Polyram Polytron A40N02 Nylon 66, 40% Long Fiber
Copyright © lookpolymers.com All Rights Reserved