Teknor Apex Telcar® OBC 4873A Thermoplastic Elastomer

Category	Polymer , Thermoplastic , Elastomer, TPE
Manufacturer	Teknor Apex Company
Trade Name	TELCAR®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Teknor Apex Telcar® OBC 4873A Thermoplastic Elastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Uses: Automotive Applications; Automotive Exterior Parts; Automotive Exterior Trim; Automotive Interior Parts; Blow Molding Applications; General Purpose; Grommets; Weatherstripping Forms: Pellets Processing Method: Extrusion; Injection Molding Injection Notes: Injection Rate: Moderate-Fast Extrusion Notes: Screw Speed: 30 to 100 rpmInformation Provided by Teknor Apex

Physical Properties	Metric	English	Comments
Specific Gravity	1.01 g/cc	1.01 g/cc	ASTM D792
Melt Flow	0.800 g/10 min @Load 2.16 kg, Temperature 230 °C	0.800 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	73	73	5 seconds; ASTM D2240
Tensile Strength at Break	7.52 MPa	1090 psi	ASTM D412
Elongation at Break	800 %	800 %	ASTM D412
Compression Set	50 % @Temperature 70.0 °C, Time 79200 sec	50 % @Temperature 158 °F, Time 22.0 hour	ASTM D395

Processing Properties	Metric	English	Comments
Rear Barrel Temperature	171 - 193 °C	340 - 380 °F
Middle Barrel Temperature	177 - 199 °C	350 - 390 °F
Front Barrel Temperature	182 - 204 °C	360 - 400 °F
Nozzle Temperature	188 - 210 °C	370 - 410 °F
Zone 1	166 - 188 °C	330 - 370 °F
Zone 2	171 - 193 °C	340 - 380 °F
Zone 3	177 - 199 °C	350 - 390 °F
Zone 5	182 - 204 °C	360 - 400 °F
Die Temperature	190 - 210 °C	374 - 410 °F
Melt Temperature	188 - 210 °C	370 - 410 °F	Processing Temperature
Mold Temperature	25.0 - 65.6 °C	77.0 - 150 °F
Injection Pressure	1.38 - 6.89 MPa	200 - 1000 psi
Back Pressure	0.172 - 0.345 MPa	25.0 - 50.0 psi
Cushion	0.381 - 2.54 cm	0.150 - 1.00 in
Screw Speed	50 - 100 rpm	50 - 100 rpm

Descriptive Properties	Value	Comments
Appearance	Opaque