Teknor Apex TEKRON® 4300-D90A Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE , Thermoplastic Elastomer, Melt-Processible Rubber |
| Manufacturer | Teknor Apex Company |
| Trade Name | TEKRON® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex TEKRON® 4300-D90A Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Teknor Apex Company
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | +/- 0.02; ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.011 cm/cm | 0.011 in/in | at 80°C for 30 min. |
| 0.012 cm/cm | 0.012 in/in | at 93°C for 30 min. | |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | at 80°C for 30 min. |
| 0.012 cm/cm | 0.012 in/in | at 93°C for 30 min. | |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
5.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 90 | 90 | 15 second delay. +/-3; ASTM D2240 |
| Tensile Strength, Yield | 8.62 MPa | 1250 psi | ASTM D412 |
| Elongation at Break | 550 % | 550 % | ASTM D412 |
| 100% Modulus | 0.00565 GPa | 0.820 ksi | ASTM D412 |
| 300% Modulus | 0.00683 GPa | 0.990 ksi | ASTM D412 |
| Flexural Modulus | 0.1060 GPa | 15.37 ksi | ASTM D790 |
| Tear Strength | 57.8 kN/m | 330 pli | Die C; ASTM D1004 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Fogging | 89, 6 hours at 95°C. (SAE-J1756) |
Users viewing this material also viewed the following:
- Polymer Resources PPX-FRG30 Modified PPO, UL 94 V-1, 30% Glass Reinforced (Unverified Data**)
- Overview of materials for Nylon, Amorphous Transparent Alloy
- KKPC Kuhmo GP 125H High Transparency GPPS
- Taiwan PU Corporation TPU-E80 General Grade, Extrusion Molding Polyester Base TPU
- Formosa Plastics Formolene® HB5502F Blow Molding HDPE
- Cosmic Plastics D72 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
- 3M 75 Repositionable Spray Adhesive
- Arlon R34661R015 0.015" (0.381 mm) Uncured Silicone Rubber with Fiberglass Substrate
- Asahi Glass Lumiflon LF-302 Solvent Soluble Fluoropolymer w/ isocyanate hardening agent
- ExxonMobil Paxon™ BA7794 Sheet Extrusion and Blow Molding Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved