Teknor Apex Monprene® MP-1349A Thermoplastic Elastomer
| Category | Polymer , Thermoplastic , Elastomer, TPE |
| Manufacturer | Teknor Apex Company |
| Trade Name | MONPRENE® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Monprene® MP-1349A Thermoplastic Elastomer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Uses: Closures; Consumer Applications; Gaskets; Handles; Kitchenware; Medical/Healthcare Applications; Packaging; Safety Equipment; Sporting Goods; Toothbrush Handles; Tubing; Writing Instruments Forms: Pellets Processing Method: Extrusion; Injection Molding Injection Notes: Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C); Injection Rate: Fast Extrusion Notes: Screw Speed: 30 to 100 rpmInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.890 g/cc | 0.890 g/cc | ASTM D792 |
| Melt Flow | 33.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
33.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 38 | 38 | ASTM D2240 |
| Tensile Strength at Break | 6.03 MPa | 875 psi | ASTM D412 |
| Tensile Stress | 2.07 MPa @Strain 300 % |
300 psi @Strain 300 % |
ASTM D412 |
| Elongation at Break | 650 % | 650 % | ASTM D412 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 182 - 232 °C | 360 - 450 °F | |
| Middle Barrel Temperature | 188 - 238 °C | 370 - 460 °F | |
| Front Barrel Temperature | 193 - 243 °C | 380 - 470 °F | |
| Nozzle Temperature | 199 - 249 °C | 390 - 480 °F | |
| Zone 1 | 182 - 232 °C | 360 - 450 °F | |
| Zone 2 | 188 - 238 °C | 370 - 460 °F | |
| Zone 3 | 193 - 243 °C | 380 - 470 °F | |
| Zone 5 | 199 - 249 °C | 390 - 480 °F | |
| Die Temperature | 199 - 249 °C | 390 - 480 °F | |
| Melt Temperature | 199 - 249 °C | 390 - 480 °F | Processing Temperature |
| Mold Temperature | 35.0 - 48.9 °C | 95.0 - 120 °F | |
| Injection Pressure | 1.38 - 5.52 MPa | 200 - 800 psi | |
| Back Pressure | 0.172 - 0.689 MPa | 25.0 - 100 psi | |
| Cushion | 0.381 - 2.54 cm | 0.150 - 1.00 in | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Clear/Transparent |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PQ 81 T 25 PP, 25% mineral filling
- Fujipoly Industries Sarcon® 85H Thin-Film HR
- LyondellBasell Petrothene® NA373242 Low Density Polyethylene, Cast/Blown Film Grade
- Solvay Polishing Opalineâ„¢
- Dow Corning SILASTIC® T-2 RTV SILICONE TRANSLUCENT BASE & CURING AGENT
- Beijing Chemical Industry KAIFA® S-206 PPS Resin
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 40 PHR Hi-Sil 243 LD Filler
- BASF Neopolen® P 9435 0.035 g/cc Core density; Expanded Polypropylene (Europe)
Copyright © lookpolymers.com All Rights Reserved