Teknor Apex Chemlon® 253 Nylon 6, Toughened

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Teknor Apex Company
Trade Name Chemlon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Teknor Apex Chemlon® 253 Nylon 6, Toughened.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features: Medium Impact Resistance; Impact modified co-polymer grade offering strength and flexibility, especially at low temperatures Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Linear Mold Shrinkage 0.015 - 0.019 cm/cm
0.015 - 0.019 in/in
ASTM D955
Melt Flow 5.00 g/10 min

@Load 1.00 kg,
Temperature 235 °C
 5.00 g/10 min

@Load 2.20 lb,
Temperature 455 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength 65.5 MPa
9500 psi
ASTM D638
Elongation at Break 50 %
50 %
ASTM D638
Elongation at Yield 5.0 %
5.0 %
ASTM D638
Flexural Strength 82.7 MPa
12000 psi
ASTM D790
Flexural Modulus 2.21 GPa
320 ksi
ASTM D790
Izod Impact, Notched 1.33 J/cm

@Temperature -40.0 °C
 2.50 ft-lb/in

@Temperature -40.0 °F
 ASTM D256
1.87 J/cm

@Temperature 22.8 °C
 3.50 ft-lb/in

@Temperature 73.0 °F
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear 84.6 µm/m-°C
47.0 µin/in-°F
ASTM D696
Melting Point 216 °C
420 °F
DSC
Deflection Temperature at 1.8 MPa (264 psi) 60.0 °C
140 °F
Unannealed; ASTM D648
UL RTI, Electrical 65.0 °C

@Thickness 0.810 mm
 149 °F

@Thickness 0.0319 in
 UL 746
65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0590 in
 UL 746
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.810 mm
 149 °F

@Thickness 0.0319 in
 UL 746
65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0590 in
 UL 746
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 UL 746
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.810 mm
 149 °F

@Thickness 0.0319 in
 UL 746
65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0590 in
 UL 746
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
 UL 746
Flammability, UL94 HB

@Thickness 0.810 mm
 HB

@Thickness 0.0319 in
Oxygen Index 21 %
21 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
ASTM D257
Dielectric Strength 11.8 kV/mm

@Thickness 3.00 mm
 300 kV/in

@Thickness 0.118 in
 ASTM D149
Comparative Tracking Index 600 V
600 V
UL 746
Processing Properties Metric English Comments
Rear Barrel Temperature 218 - 235 °C
425 - 455 °F
Middle Barrel Temperature 229 - 252 °C
445 - 485 °F
Front Barrel Temperature 241 - 260 °C
465 - 500 °F
Nozzle Temperature 241 - 266 °C
465 - 510 °F
Melt Temperature 241 - 266 °C
465 - 510 °F
Processing Temperature
Descriptive Properties Value Comments
Suggested Moisture, max 0.2
Suggested Regrind, max 25