SABIC Innovative Plastics SABIC PPCOMPOUND 5521 PP
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC PPCOMPOUND |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics SABIC PPCOMPOUND 5521 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® PPcompound 5521 is a mineral filled, impact modified polypropylene TPO. This material combines good flow with exterior automotive weathering stability. The general purpose black color product is offered without weathering stability for good paintability. The weatherable product was originally designed for unpainted automotive exterior bumper cap and step pad applications where high flexibility is required. The IMDS is 163257209.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.900 g/cc | 0.900 g/cc | ASTM D792 |
| Density | 0.900 g/cc | 0.0325 lb/in³ | ISO 1183 |
| Melt Flow | 19 g/10 min <br>@Load 2.16 kg,<br> Temperature 230 °C |
19 g/10 min <br>@Load 4.76 lb,<br> Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 57 | 57 | ISO 868 |
| Tensile Strength at Break | 13.0 MPa | 1890 psi | 50 mm/min, 1A; ISO 527 |
| Tensile Strength, Yield | 18.0 MPa | 2610 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 160 % | 160 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 0.850 GPa | 123 ksi | 1 mm/min; ISO 527 |
| Flexural Modulus | 0.890 GPa | 129 ksi | 2 mm/min, 64mm span; ISO 178 |
| Izod Impact, Notched (ISO) | 49.0 kJ/m² | 23.3 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| 9.00 kJ/m² <br>@Temperature -30.0 °C |
4.28 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| 11.0 kJ/m² <br>@Temperature 0.000 °C |
5.23 ft-lb/in² <br>@Temperature 32.0 °F |
80*10*4mm, Cut; ISO 180/1A | |
| Charpy Impact, Notched | 5.90 J/cm² | 28.1 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 0.700 J/cm² <br>@Temperature -30.0 °C |
3.33 ft-lb/in² <br>@Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| 1.10 J/cm² <br>@Temperature 0.000 °C |
5.23 ft-lb/in² <br>@Temperature 32.0 °F |
80*10*4mm, Cut; ISO 179/1eA | |
| Dart Drop, Total Energy | 17.0 J <br>@Temperature 23.0 °C |
12.5 ft-lb <br>@Temperature 73.4 °F |
Instrumented Impact Energy @ peak, 6.6 m/s; ASTM D3763 |
| 23.0 J <br>@Temperature -30.0 °C |
17.0 ft-lb <br>@Temperature -22.0 °F |
Instrumented Impact Energy @ peak, -30°C @ 2.2 m/s; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 129 µm/m-°C <br>@Temperature -30.0 - 100 °C |
71.7 µin/in-°F <br>@Temperature -22.0 - 212 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 148 µm/m-°C <br>@Temperature -30.0 - 100 °C |
82.2 µin/in-°F <br>@Temperature -22.0 - 212 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C | 187 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| Vicat Softening Point | 136 °C | 277 °F | 10N, 50°C/hr; ISO 306 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 0405 Polypropylene
- Parker Chomerics CHO-FLEX 601 Conductive Coating
- Fiberfil® J-60/40/E/EX Polypropylene Homopolymer, 40% Glass Reinforced, Chemically coupled, high viscosity
- Kinetics MIM K3 Heat Treat
- Lucent Polymers PC/PBT-1430U Polycarbonate+PBT, Superior Weatherability, Injection Grade
- Karina E 837-10/168-A-ERYB-AS White PVC Compound
- Ferro CF 7574 Glaze and Sealant Glass
- Kuraray SEPTON® S45 Soft Compound
- A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66
- CMW® ELKONITE 30SB tungsten, silver
Copyright © lookpolymers.com All Rights Reserved