Teknor Apex Chemlon® 182 Nylon 66, Non-Halogenated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced, Flame Retardant |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 182 Nylon 66, Non-Halogenated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: General Purpose; U.L. 94 V-O at 0.57 mm; Colorable; Flame Retardant Processing Method: Injection Molding Forms: PelletsInformation Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 - 0.014 cm/cm | 0.0090 - 0.014 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 72.4 MPa | 10500 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 103 MPa | 15000 psi | ASTM D790 |
| Flexural Modulus | 3.21 GPa | 465 ksi | ASTM D790 |
| Izod Impact, Notched | 0.534 J/cm @Temperature 22.8 °C |
1.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 257 °C | 495 °F | DSC |
| Deflection Temperature at 0.46 MPa (66 psi) | 224 °C | 435 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | Unannealed; ASTM D648 |
| UL RTI, Electrical | 120 °C @Thickness 0.810 mm |
248 °F @Thickness 0.0319 in |
UL 746 |
| 120 °C @Thickness 1.50 mm |
248 °F @Thickness 0.0590 in |
UL 746 | |
| 120 °C @Thickness 3.00 mm |
248 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical with Impact | 95.0 °C @Thickness 0.810 mm |
203 °F @Thickness 0.0319 in |
UL 746 |
| 105 °C @Thickness 1.50 mm |
221 °F @Thickness 0.0590 in |
UL 746 | |
| 105 °C @Thickness 3.00 mm |
221 °F @Thickness 0.118 in |
UL 746 | |
| UL RTI, Mechanical without Impact | 120 °C @Thickness 0.810 mm |
248 °F @Thickness 0.0319 in |
UL 746 |
| 120 °C @Thickness 1.50 mm |
248 °F @Thickness 0.0590 in |
UL 746 | |
| 120 °C @Thickness 3.00 mm |
248 °F @Thickness 0.118 in |
UL 746 | |
| Flammability, UL94 | V-0 @Thickness 0.569 mm |
V-0 @Thickness 0.0224 in |
|
| Oxygen Index | 33 % | 33 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 16.9 kV/mm @Thickness 3.00 mm |
430 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 600 V | 600 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 246 - 257 °C | 475 - 495 °F | |
| Middle Barrel Temperature | 263 - 268 °C | 505 - 515 °F | |
| Front Barrel Temperature | 263 - 274 °C | 505 - 525 °F | |
| Nozzle Temperature | 268 - 279 °C | 515 - 535 °F | |
| Melt Temperature | 263 - 277 °C | 505 - 530 °F | Processing Temperature |
| Drying Temperature | 79.4 °C | 175 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Suggested Moisture, max | 0.2 |
Users viewing this material also viewed the following:
- PolyOne LubriOne™ AT-000/10T 2S Acetal (POM) Copolymer
- Network Polymers Softflex® UB 30 Black OEX
- Solvay Specialty Polymers Cogegum® AFR/920 Polyolefin, Unspecified (discontinued **)
- PTS Tristar® PC-08 8 MFI Extrusion Grade Polycarbonate
- UBE 5033T Nylon 6/66 Monofilament (Drawing Ratio=5)
- Polyram RamOfin PPH307G6 Polypropylene, 30% Glass Fiber
- Addiplast Addinyl PMD 20104 Nylon 66
Copyright © lookpolymers.com All Rights Reserved