Teknor Apex Chemlon® 104-13 GH Nylon 66, 13% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Teknor Apex Company |
| Trade Name | Chemlon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teknor Apex Chemlon® 104-13 GH Nylon 66, 13% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Notes: Impact Modified; Reinforced with 13% Glass Fibers; Synergistic compound exhibiting impact strength and dimensional stability Features: Good Dimensional stability; Good Processability; Heat Stabilized; Good Impact Resistance; Good Toughness; High Strength Processing Method: Injection Molding Forms: PelletsAdditive: Heat Stabilizer Automotive Specifications: Chrysler MS-DB41 CPN1987 Color: BK001 Black; Ford ESA-M4D189-A; GM GMP.PA66.057Information Provided by Teknor Apex
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hr; ASTM D750 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | ASTM D955 |
| Melt Flow | 20.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
20.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 96.5 MPa | 14000 psi | ASTM D638 |
| Elongation at Break | 7.0 % | 7.0 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Strength | 134 MPa | 19500 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm @Temperature -40.0 °C |
1.30 ft-lb/in @Temperature -40.0 °F |
ASTM D256 |
| 1.33 J/cm @Temperature 22.8 °C |
2.50 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.810 mm |
HB @Thickness 0.0319 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Strength | 111 kV/mm @Thickness 3.00 mm |
2820 kV/in @Thickness 0.118 in |
ASTM D149 |
| Comparative Tracking Index | 500 V | 500 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 241 - 257 °C | 465 - 495 °F | |
| Middle Barrel Temperature | 263 - 274 °C | 505 - 525 °F | |
| Front Barrel Temperature | 263 - 282 °C | 505 - 540 °F | |
| Nozzle Temperature | 263 - 279 °C | 505 - 535 °F | |
| Melt Temperature | 257 °C | 495 °F | |
| 263 - 279 °C | 505 - 535 °F | Processing Temperature | |
| Mold Temperature | 60.0 - 93.3 °C | 140 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Screw Speed | 60 - 120 rpm | 60 - 120 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Black; Natural Color | |
| Suggested Moisture, max | 0.2 | |
| Suggested Regrind, max | 25 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible R100AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- Chevron Phillips Marlex® HHM 5202 Polyethylene, Sheet/Thermoforming Grade, HDPE (discontinued **)
- Materion BrushCAST® 275CT Fine Grain Casting Alloy (Solution Annealed & Aged)
- Industrial Laminates/Norplex NP310E Cotton Fabric
- SABIC Innovative Plastics LNP LUBRICOMP DZL24 PC
- Goodfellow Copelmet® Tungsten 72/Copper 28 Alloy
- Covestro Bayblend® KU 2-1500 Polycarbonate/ABS Blend
- ExxonMobil SpectraSyn™ 10 Polyalphaolefin (PAO) Fluid
- Arlon 0.028" (0.7112 mm) Flexible Heater Silicone with Fiberglass Substrate (55586R028)
- PolyOne Syncure™ S1060A Polyethylene, Crosslinked (XLPE)
Copyright © lookpolymers.com All Rights Reserved