Chosun Refractories HSC-17 Dense and High-Strength Castable, Credens
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories HSC-17 Dense and High-Strength Castable, Credens.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.010791 GPa @Temperature 110 °C, Time 86400 sec |
1.5651 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.011772 GPa @Temperature 1000 °C, Time 10800 sec |
1.7074 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.012753 GPa @Temperature 1500 °C, Time 10800 sec |
1.8497 ksi @Temperature 2730 °F, Time 3.00 hour |
||
| Compressive Strength | 63.7 MPa @Temperature 110 °C, Time 86400 sec |
9250 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 66.7 MPa @Temperature 1000 °C, Time 10800 sec |
9670 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 80.4 MPa @Temperature 1500 °C, Time 10800 sec |
11700 psi @Temperature 2730 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1700 °C | 3090 °F | limited |
| Shrinkage | -0.400 % @Temperature 1500 °C, Time 10800 sec |
-0.400 % @Temperature 2730 °F, Time 3.00 hour |
|
| -0.0500 % @Temperature 110 °C, Time 86400 sec |
-0.0500 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 75 % | 75 % | |
| CaO | 2.0 % | 2.0 % | |
| SiO2 | 20 % | 20 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 120 - 600 min | 2.00 - 10.0 hour | Setting Time |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Vibrating, Casting | |
| Material Required for Estimating(kg/?) | 2,750 | |
| Water Required for Casting(%) | 6 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible C7000 Polyvinyl Chloride, Flexible (PVC, Flexible)
- Solvay Specialty Polymers Halar® 350LC Polyethylene, Chlorotrifluoroethylene (ECTFE) (Unverified Data**)&
- Kazanorgsintez M 168 Polymer Composition for Rotary Molding
- Lehmann & Voss LUVOCOM® 20-7687 Polyphthalamide, with aramid reinforcement and PTFE
- SABIC Innovative Plastics LNP LUBRICOMP KFP032 Acetal Copolymer (Asia Pacific)
- Borealis GB364WG Polypropylene Compound, Glass Fiber Reinforced
- Dow Corning 5103 Surfactant
- Addcomp ADD-VANCE® DS 485 Desiccant masterbatch in LLDPE carrier
- Tra-Con Tra-Bond 2138 Easy-Flow No-Sag Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved