Teijin Multilon TN-7000 Halogen-Free Flame Resistant PC/ABS Polymer Alloy
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Teijin |
| Trade Name | Multilon |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Teijin Multilon TN-7000 Halogen-Free Flame Resistant PC/ABS Polymer Alloy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Halogen-free flame retardant PC/ABS polymer alloy, and is also antimony-free. It is a typical type with high flowability, light resistance and heat stability that is suitable for a business machine chassis etc..Information provided by Teijin Chemicals Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
|
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0060 cm/cm @Thickness 4.00 mm |
0.0040 - 0.0060 in/in @Thickness 0.157 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 48.0 MPa | 6960 psi | 50mm/min; ISO 527 |
| Tensile Strength, Yield | 63.0 MPa | 9140 psi | 50mm/min; ISO 527 |
| Elongation at Break | 80 % | 80 % | 50mm/min; ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | 50mm/min; ISO 527 |
| Flexural Strength | 95.0 MPa | 13800 psi | 2mm/min; ISO 178 |
| Flexural Modulus | 2.60 GPa | 377 ksi | 2mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
ISO 11359 |
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ISO 75 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VA @Thickness 2.00 mm |
5VA @Thickness 0.0787 in |
Users viewing this material also viewed the following:
- Minelco FordaCal
- Minelco DekorLux
- Momentive Performance Materials HV 3/506 Heat Cured Rubber - High Temperature
- Saint-Gobain Chemfab® q-GUARD® 18 Insulation Jacketing
- Techmer ES HiFill® PP GB40 40% Glass Beads Filled
- Borealis FA7220 Low Density Polyethylene
- Hexcel® HexPly® 954-6 Curing Cyanate Resin, M40J Fiber
- Arlon R36580N015 0.015" (0.381 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
Copyright © lookpolymers.com All Rights Reserved